Search Results

Carburized and quenched materials with high fatigue strength are often used for motorcycle engine parts. Nitrided materials exhibit less deformation during heat treatment than carburized and quenched materials, so if the same or higher fatigue strength can be achieved with nitrided materials as with carburized and quenched materials, the geometric precision of parts can be increased and we can reduce engine noise as well as power loss. When the fatigue strengths of a nitrided material with its compound layer surface put into γ’ phase through nitriding potential control (hereafter, G), and a nitrided material put into ε phase (hereafter, E) were measured, the results showed the fatigue strength of the G to be about 11% higher than that of carburized and quenched materials. It was inferred that the strength of the compound layer determines fatigue strength.

A connecting rod made of titanium alloy is effective for lower fuel consumption and higher power output comparing to a steel one because the titanium connecting rod enables to reduce the weight of both of reciprocating and rotating parts in an entire engine substantially. But up to now, it has been adopted only to expensive and small-lot production models because a material cost is high, a processing is difficult and a wear on a sliding area should be prevented. In order to adopt the titanium connecting rods into a more types of motorcycles, appropriate materials, processing methods and surface treatment were considered. Hot forging process was applied not only to reduce a machining volume but also to enhance a material strength and stiffness. And the fracture-splitting (FS) method for the big-end of the titanium connecting rod was put into a practical use.

In four-cycle single-cylinder motorcycle engines, high Hertzian stress is generated on and beneath the big-end surface of the connecting rod. If the surface strength would be improved, the diameter of the big-end could be made smaller, making the entire engine smaller and lighter. Therefore, application of carbide dispersion carbonitriding using a vacuum furnace (hereinafter referred to as “vacuum CD carbonitriding”) on the big-end surface was investigated. Vacuum CD carbonitriding was carried out by three processes. The first was a CD carburizing process. This process is done to obtain granular cementite, but in order to avoid decreasing the strength, it is necessary to prevent the formation of coarsened cementite at the grain boundary. The second process was a refining process. This process is done for the purpose of refining the prior austenite grain size. The third process was a carbonitriding process.

This paper describes an experimental method to predict the rolling contact fatigue life of a crankpin in a market vehicle engine. The fatigue life up to pitting was evaluated by two laboratory tests including a fatigue life measurement using a ball-on-disk test machine and a crankpin durability measurement by an engine bench test. The surface observation after the tests revealed that the surface dent triggers pitting in both tests. The Weibull plot of the percent failure vs. cycle to failure as a function of the contact stress was presented. In order to directly evaluate the effect of the contact stress on the lifetime, the lifetime values measured at L50 are plotted in the diagram showing the contact stress vs. cycle to failure. The obtained relation can predict the lifetime under the controlled condition in which the number of maximum torque points is countable.

The fracture splitting (FS) method for case hardened connecting rods has been developed to improve engine performance while decreasing production costs. The FS method is widely used for automotive connecting rods because it effectively improves their productivity. Normalized forging steels, microalloyed forging steels and powder metals have generally been used as the material in the FS method as they are easily split due to their brittleness. On the other hand, the materials to be used for high performance motorcycles are case hardened low carbon steels because they allow the connecting rods to be lightweight due to their high fatigue strengths. These materials, which have a hardened area of approx. 0.5mm in depth from the surface, have a ductile texture inside. This texture obstructs the crack propagation and makes the split force too high to split without deforming the bearing area.

A control system for auto driving of motorcycle using anthropomorphic robot has been developed to efficiently evaluate a motorcycle with high accuracy, the performance of which is becoming higher. For magnetostriction-type load sensor, which is absolutely necessary for this system, the strain gauge type load cell has been used conventionally. However, the detection sensitivity, strength, and responsibility have not been satisfied completely under engine vibration conditions. To solve this problem, a magnetostriction-type load sensor has been newly developed. As a result of the tests with actual machines, it is found that this magnetostriction-type load sensor satisfies the conditions necessary for the motorcycle drive control system and measurement system.

The Bonded Valve Seat System is the latest technology to realize drastic reduction in valve temperature in SI engines characterized by the good thermal conductivity of extremely thin valve seats bonded directly on the aluminum cylinder head. A unique and highly rationalized resistance bonding technique was developed to maintain adequate bonding strength and positioning precision in a short bonding period of around one second. Engineering data on optimization of bonding-section geometry, valve seat material and the surface treatment and bonding parameters were presented and discussed regarding the mechanism. The geometry of the bonding section of the cylinder head was optimized by FEM analysis so that the aluminum material should deform to embed the valve seat ring with the action of expelling the surface contamination and the oxide film. The bonding facility was modified so that the electrode axis should move flexibly according to distortion of the cylinder head during bonding.