Standard

Aluminum Alloy, Plate (7160-T7451), 7.0Zn – 2.2Cu – 1.5Mg - 0.10Zr, Solution Heat Treated, Stress Relieved, and Overaged

2024-03-08

WIP

AMS4432A

This specification covers an aluminum alloy in the form of plate 1.000 to 6.000 inch (25.40 to 152.40 mm), inclusive, in nominal thickness (see 8.4).

Standard

Aluminum Alloy, Alclad Sheet, 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (Alclad 7050-T76), Solution Heat Treated and Overaged

2024-03-08

WIP

AMS4243D

This specification covers an aluminum alloy in the form of alclad sheet 0.040 to 0.187 inch (1.02 to 4.75 mm) inclusive in nominal thickness (see 8.6).

Standard

Aluminum Alloy, Extrusion 3.7 Cu-1.15 Li - 0.50 Zn -0.40 Mg, 0.30 Mn - 0.10 Zr Solution Heat Treated, Stress Relieved by Stretching 2% to 5% and Aged

2024-03-08

WIP

AMS4257A

This specification covers an aluminum alloy in the form of extruded bars, rods, and profiles.

Standard

Aluminum Alloy Extrusions, 7.9Zn - 1.6Cu - 2.2Mg - 0.16Cr (7249-T76511), Solution Heat Treated, Stress-Relieved, Straightened, and Overaged

2024-03-08

WIP

AMS4293B

This specification covers an aluminum alloy procured in the form of extruded bars, rods, wire, profiles (shapes) and tubing up to 1.499 inches (38.07 mm), inclusive in nominal diameter or least thickness (bars, rods, wire, profiles) or nominal wall thickness (tubing) (see 8.6).

Standard

Minimization of High Temperature Oxidation, Aluminum Alloy Heat Treatment

2024-03-08

WIP

ARP7500A

This recommended practice provides recommendations for minimizing high temperature oxidation (HTO) during the heat treatment of aluminum alloy products and parts. HTO leads to deterioration of properties.

Standard

Aluminum Alloy, Castings, 5.0Si - 1.2Cu - 0.50Mg (C355.0-T6), Solution and Precipitation Heat Treated

2024-03-08

WIP

AMS4215K

This specification covers an aluminum alloy in the form of sand, permanent mold, composite mold, and investment castings.

Standard

Aluminum Alloy, Plate (7065-T7651), 7.7Zn - 2.1Cu - 1.65Mg - 0.10Zr, Solution Heat Treated, Stress-Relieved, and Overaged

2024-03-08

WIP

AMS4351B

This specification covers an aluminum alloy in the form of plate.

Standard

Aluminum Alloy, Alclad Sheet and Plate, 6.3Cu - 0.30Mn - 0.18Zr - 0.10V - 0.06Ti, Alclad 2219-T31; Sheet, Solution Heat Treated and Cold Worked, Alclad 2219-T351; Plate, Solution Heat Treated and Stress Relieved

2024-03-08

WIP

AMS4095F

This specification covers an aluminum alloy in the form of sheet and plate 0.020 to 0.499 inch (0.51 to 12.67 mm) inclusive, in nominal thickness (see 8.4) alclad two sides.

Standard

Aluminum Alloy, Extruded Rod, Bar and Profiles (7055-T74511), 8.0Zn - 2.3Cu - 2.0Mg - 0.16Zr, Solution Heat Treated, Stress-Relieved, and Overaged

2024-03-08

WIP

AMS4324C

This specification covers an aluminum alloy in the form of extruded bars, rods, and profiles (shapes) produced with a cross sectional area of 24 square inches (155 square centimeters) maximum and a circumscribing circle (see 8.3) diameter (circle size) of 10.5 inches (267 mm) maximum, with a nominal thickness up to 3.000 inch (76.20 mm), inclusive (see 8.6).

Standard

Aluminum Alloy, Extrusions 1.0Mg - 0.60Si - 0.30Cu - 0.20Cr (6061-T6511) Solution Heat Treated, Stress Relieved by Stretching, Straightened, and Precipitation Heat Treated

2024-03-08

WIP

AMS4173H

This specification covers an aluminum alloy in the form of extruded bars, rods, wire, profiles, and tubing. These extrusions have been used typically for parts requiring moderate strength and where distortion during machining must be minimized, but usage is not limited to such applications.

Standard

Aluminum Alloy, Rolled or Cold Finished Bars and Rods, (7075-T651), Solution and Precipitation Heat Treated

2024-03-04

CURRENT

AMS4123L

This specification covers an aluminum alloy in the form of bars and rods in the sizes and shapes described in 3.3.1 (see 8.7).

Standard

Aluminum Alloy Tubing, Seamless, Drawn 1.8Cu - 1.0Mg - 0.8Si - 0.20Cr Solution Heat Treated, Stress-Relieved by Stretching, and Aged (2013-T6511)

2024-03-01

CURRENT

AMS4002B

This specification covers an aluminum alloy in the form of seamless, drawn tubing having nominal wall thickness of 0.120 to 0.400 inch (3.00 to 10.00 mm), inclusive (see 8.5).

Standard

Aluminum Alloy, Sheet and Plate, 6.3Cu - 0.30Mn - 0.06Ti - 0.10V - 0.18Zr, Solution Heat Treated, Cold Worked (8%) and Naturally Aged (2219 -T37)

2024-03-01

CURRENT

AMS4600B

This specification covers an aluminum alloy in the form of sheet and plate 0.020 to 5.000 inches (0.51 to 127.00 mm) in nominal thickness (see 8.5).

Standard

Aluminum Alloy, Forgings and Rolled or Forged Rings, (6061-T6), Solution and Precipitation Heat Treated

2024-03-01

CURRENT

AMS4127L

This specification covers an aluminum alloy in the form of die forgings not over 4 inches (102 mm) in nominal thickness at time of heat treatment , hand forgings with as-forged thickness not exceeding 8 inches (203 mm) and the cross-sectional area not greater than 256 square inches (1652 cm2), forged or rolled rings 3.5 inches (89 mm) and under in nominal thickness at time of heat treatment and having an OD-to-wall thickness ratio of 10:1 or greater, and stock of any size for forgings and rings (see 8.6).

Standard

Aluminum Alloy, Centrifugal Castings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (709.0-T61) Hot Isostatically Pressed, Solution and Precipitation Heat Treated

2024-02-27

CURRENT

AMS4406B

This specification covers an aluminum alloy (see 8.5) in the form of centrifugal castings.

Standard

Brass Tubing, Seamless, 66.5Cu - 33Zn - 0.45Pb, Annealed

2024-02-13

WIP

AMS4554D

This specification covers one grade of brass in the form of seamless tubing.

Standard

Forgings, Magnesium Alloy, 5.5Zn - 0.45Zr (ZK60A-T5), Precipitation Heat Treated

2024-02-13

WIP

AMS4362J

This specification covers a magnesium alloy in the form of die forgings 3 inches (76 mm) and under in nominal thickness at time of heat treatment, hand forgings 6 inches (152 mm) and under in nominal thickness, and forging stock of any size (see 8.5).

Standard

Aluminum Alloy, Sheet and Plate, Alclad, 4.4Cu - 1.5Mg - 0.60Mn (2024, -T3 Sheet/-T351 Plate with 1-1/2% Alclad), Solution Heat Treated, Cold Worked and Naturally Aged

2024-02-13

WIP

AMS4041U

This specification covers an aluminum alloy in the form of sheet and plate alclad two sides, over 0.187 to 1.000 inch (over 4.750 to 25.40 mm) in nominal thickness, supplied in the -T3/-T351 temper.

Standard

Aluminum Alloy Bars, Rods, and Wire Rolled or Cold Finished, and Rings, 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T6, 7075-T651), Solution and Precipitation Heat Treated

2024-02-13

WIP

AMS4122N

This specification covers an aluminum alloy in the form of rolled or cold finished bars, rods, and wire, and of flash welded rings conforming to the dimensions listed in Table 2 (see 8.4).

Standard

Aluminum Alloy, Alclad Sheet, 4.4Cu - 1.5Mg - 0.60Mn (Alclad 2024-O), Annealed, Fine Grain

2024-02-13

WIP

AMS4274C

This specification covers an aluminum alloy in the form of sheet 0.009 to 0.126 inch (0.23 to 3.20 mm) inclusive, in nominal thickness, alclad.