This paper provides a review of the fatigue properties reported in the open literature for die cast magnesium-based alloys. Recently developed fatigue data, in the form of stress versus number of cycles to failure for bending fatigue (R=-1), are presented for die cast AM60B and AZ91D alloy specimens with thicknesses between 1 and 10 mm. The effects of specimen thickness and macrostructural features, such as porosity distributions and surface features (parting line and ejection pin marks), on the fatigue data are discussed.

Reported tensile and fatigue properties of die cast AZ91D and AM60B magnesium alloys indicate that those values depend on the size and shape of the test samples and their global porosities. This paper reviews the mechanical properties reported in the open literature for these die cast alloys and indicates that section thickness and global porosity are inadequate for predicting the tensile and fatigue properties of die cast AZ91D and AM60B magnesium alloys.

Die cast AZ91D and AM60 magnesium alloy components are finding increasing usage in automotive applications. Both hot and cold chamber die cast components of these alloys generally exhibit several common microstructural features, including “skin”, porosity banding, and porosity distributed about the component centerline. Methods for quantitatively characterizing these microstructural features are described and representative values for skin thicknesses, porosity band dimensions and porosity band locations from selected die castings will be presented. The expected influence of these common microstrucutral features on mechanical properties and acceptability of die cast magnesium components for given applications are discussed.

Magnesium anodizing processes have been reported to affect the strength of the underlying metal adversely so that service lives of components may be reduced. It has been suggested that localized surface heating effects during anodization may be responsible for introducing defects in the metal surface which may then result in a degradation of mechanical properties. While there is a need for more extensive research in this area, recent studies have shown that at least one magnesium anodizing process may in fact assist in achieving more favorable mechanical properties in magnesium die castings.