Reduction in Weight of Steel Wheels by Development of 780 MPa-Grade Hot Rolled Steel Sheets 940536

Two new types of high-strength 780 MPa-grade hot rolled steel sheets were developed for use in wheel discs and rims, which are the structural parts of the wheel.
The fundamental composition of the disc material is 0.08%C-1.5%Si-1.75%Mn-0.1%Ti. The basic material is a dual phase, ferrite-martensite steel, with precipitation strengthening of the soft ferrite phase by TiC. The aim of hardening the ferrite phase is to suppress the difference in hardness between the ferrite and martensite phases, and thus secure good stretch flangeability.
The fundamental composition of the rim material is 0.09%C-1.7%Mn-0.05%Nb-0.15%Ti. This steel is based on a ferrite-bainite material and is precipitation strengthened using NbC and TiC.
Although 590 MPa-grade steel had been considered to represent the limit of formability for wheels, a 30% increase in strength was achieved in the newly developed materials, while maintaining good formability. This makes it possible to reduce the thickness of discs and rims and achieve a reduction of approximately 10% in wheel weight.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 16% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Spot Weldability and Fatigue Property of Hot-Rolled High-Strength Sheet Steels for Wheel Usage

880374

View Details

TECHNICAL PAPER

High Strength Steels for Wheel Use

880695

View Details

TECHNICAL PAPER

Properties of Induction Heat-Treated High-Strength Spring Wire

830656

View Details

X