Effect of Coating Structure on Powdering Resistance of Galvannealed Steel Sheet 920174

Galvannealed steel sheets containing 10wt%Fe in coated layer were prepared in various galvannealing temperature and cooling rate. Powdering resistances were evaluated by a draw bead test. X-ray diffraction examination revealed an attribution of the coating structure to powdering resistance.
Higher galvannealing temperature(500∼550°C) deteriorates powdering resistance, but slower cooling from higher temperature improves it. At low galvannealing temperature(440°C), powdering resistance is rather good independent of cooling rate. Г1-phase(Fe5Zn21) is formed along the interface between coating and steel when samples are galvannealed at lower temperature(≦500°C) or cooled at slower cooling rate from higher galvannealing temperature. The results suggest that the increase of Г1 ratio [Г1/(Г+Г1)] in the coating is inclined to improve powdering resistance.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 16% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Influence of Strain State on Powdering of Galvannealed Sheet Steel

960026

View Details

TECHNICAL PAPER

The Peeling-Off Resistance of Zinc and Iron-Zinc Coated Steel Sheets in Stamping

890349

View Details

TECHNICAL PAPER

Correlation of Prephosphate Treatment, Surface Friction and Powdering of Galvanneal During Forming

980075

View Details

X