Automotive Magnesium Die Casting Through Thermal and Flow Control 2005-01-0329

Some causes for hot cracking in automotive magnesium casting were studied through thermal and fluid flow analysis. Solidification of magnesium alloy casting is found to start early, but complete late. There are small amount of residual liquid phase staying at the eutectic temperature. This property is the main reason that magnesium castings crack. The different solidification defect patterns between the center and skin of castings are analyzed. Some crack prevention techniques and criteria are introduced to obtain better solidification pattern, which leads to higher quality castings.
Separation and filling reversal are also frequently causing magnesium castings to crack. Through the study of the flow atomization number and the Reynolds number, the magnesium casting filling process is found to be a typical turbulent flow process. The optimized flow pattern with necessary design changes is introduced to generate better flow results during mold filling.
Several real automotive magnesium die casting parts are used as examples, coupled with some thermal and fluid flow concepts, tables and process simulations results to illustrate the positive and negative experiences in the automotive magnesium die casting manufacturing.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 16% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Optimizing the Magnesium Die Casting Process to Achieve Reliability in Automotive Applications

2005-01-0333

View Details

TECHNICAL PAPER

Effects of Section Size and Microstructural Features on the Mechanical Properties of Die Cast AZ91D and AM60B Magnesium Alloy Test Bars

1999-01-0927

View Details

TECHNICAL PAPER

Permanent Mold Casting and Creep Behavior of Mg - 4 Al - 4 X: (Ca, Ce, La, Sr) Alloys

2007-01-1027

View Details

X