Galvanic corrosion between die cast AZ91D and AM60B and different fastener systems has been evaluated by exposure on trucks and in accelerated laboratory tests. The exposure time on the trucks was 3 years, corresponding to a mileage of about 300000 km. Samples were retracted and evaluated after 1 and 2 years exposure. Similar samples were also exposed to the Volvo Indoor Corrosion Test and the General Motors GM9540P-cycle B test. The correlation between the field data and the laboratory tests was evaluated, as was the sharp difference in the performance of the fastener systems in the two accelerated laboratory tests.

Galvanic corrosion of high purity die cast magnesium alloys AM50 and AZ91 was examined in accelerated atmospheric corrosion testing according to Volvo STD 1027,1375 for 6 weeks involving cycling of the relative humidity between 90% and 45% in combination with intermittent immersion in one of two NaCl-solutions (0.3% or 1.0%). The exposures were performed at two different CO2 levels; 0.01% and 0.3%. The initial general corrosion rate of the AM50 alloy is 50-100% higher than that of AZ91 depending on surface preparation. The corrosion weight loss of both materials depends linearly on salt load in the investigated range. CO2 has a moderate accelerating effect, being higher with decreased salt load. Extreme value analysis was used to evaluate the deepest pit distribution around the perimeter of mounted bolts in panels of AZ91 and AM50. Quite contrary to the general corrosion results, AZ91 showed 30% deeper pits than AM50.