At Mitsubishi Motors, a thin-walled exhaust manifold, made of stainless cast-steel, has been developed with the aim of achieving higher heat-resisting reliability as well as weight reduction. The new exhaust manifold is made of ferritic stainless cast-steel, employing an advanced vacuum casting (CLAS). Its geometry was designed using finite element analysis and its durability was confirmed by testing both on various test devices and on a vehicle. The exhaust manifolds has been adopted on a production engine model and has proven the following advantages over a conventional cast-iron ones; excellent heat resistance. weight reduction of over 20%. possible exhaust emission reduction as a result of lower heat-capacity of the exhaust manifold.

Beta Ti alloy valve spring retainers are newly developed for use in mass produced automobiles for the first time. Ti alloy valve spring retainers vith a weight saving of 42%, compared to steel retainers, have reduced the inertial weight of the valve train components by 6%. And this weight reduction has the benefit of increasing the upper limit of the engine speed, which improves the engine performance. Ti alloy valve spring retainers are cold forged by the conventional fabrication facilities for steel retainers, using Ti-22V-4Al (the beta Ti alloy) which possesses excellent cold workability in a solution treated condition. Oxygen surface hardening is applied to protect Ti alloy valve spring retainers from wear damage. In addition, aging treatment and shot blasting are performed to improve strength and stiffness of valve retainers.