Search Results

The feasibility of using ceramic catalytic converters to reduce HC and CO emissions from 2-stroke motorcycles and scooters was investigated by performing mass emission tests on the Indian Driving Cycle. It was found that it is possible to reduce emissions significantly by installing ceramic catalytic converters at a proper location in the exhaust pipe. A power loss requirement of <5% was also met with ceramic converters. Laboratory tests on mat durability indicated that the ceramic catalytic converter package can offer excellent mechanical durability under Indian driving conditions.

New test methods were developed to characterize the high temperature durability of intumescent mats that are used to mount ceramic catalyst supports in stainless steel cans. The key attribute of these tests is the use of an electric resistance heating method to maintain a temperature gradient through the thickness of the mat when a cyclic or constant shear stress is applied to the mat interface. These tests are simple to perform and do not require expensive equipment or highly skilled operators. Using these new test methods, the durability of ceramic preconverters mounted with 4070 gm/m2 intumescent mat was studied. The results of these tests indicate that a preconverter package with 4070 gm/m2 intumescent mat can perform satisfactorily in the close-coupled application where temperatures exceed 900°C. The mat performance can be quantified in terms of applied stress and test temperature by utilizing the experimental methods described in the present study.

Motorcycle exhaust emission standards throughout the world are becoming more stringent. Emission control systems utilizing the catalytic converter are already in production in Taiwan for 2-stroke engine motorcycles. Catalysts designed for 2-stroke engines encounter a more severe exhaust environment than do those designed for 4-stroke engines. The two aspects of increased severity are the higher temperatures and higher stresses due to engine vibrations. Precious metal catalysts have been designed to operate in the thermal environment of 2-stroke engines and such catalysts have been successfully applied to both metal and ceramic substrates. However, until now, only the metal substrate catalysts have been utilized in motorcycle application. Ceramic based catalysts have not been considered because the mounting material that holds the catalyst substrate in place did not have enough durability to withstand the thermal/vibrational forces encountered in 2-stroke engine exhaust.

High temperature modulus of rupture (MOR) data, published previously, show that the ceramic catalyst supports get stronger with temperature due to the absence of water vapor and closure of microcracks which would otherwise act as stress concentrators [1, 2 and 3]*. The increased MOR value is partially responsible for the excellent durability of ceramic catalyst supports at high temperature. In this paper, we will present the compressive strength data of ceramic substrates at high temperature, namely the crush strength along B-axis and biaxial compressive strength of the whole substrate. Since the honeycomb strength is directly related to that of the individual cell wall, the compressive strength should also increase with temperature similar to the modulus of rupture. Accordingly, the ceramic substrates are capable of supporting higher mounting pressures exerted by the intumescent mat at high temperature [4].

The design, performance and optimization of the extruded electrically heated metal converter have recently been published(1,2). The present paper focuses on the physical durability of extruded metal EHC support at high temperature representative of operating conditions. The mechanical, thermal, creep and fatigue properties of Fe-Cr-Al honeycomb structure over 25°-1000°C temperature range are reported. In addition, the stresses arising from mounting and thermal loads are computed via finite element analysis and compared with the high temperature strength of extruded metal EHC support. A safe design stress which predicts 192,000 kilometer durability is estimated from high temperature fatigue behavior of extruded Fe-Cr-Al honeycomb structure.

Since their introduction to automotive industry in 1975, ceramic substrates have successfully met the strength requirements for canning, engine and chassis vibrations, and thermal shock. This paper will focus on canning loads and techniques, and how they influence the stress distribution in ceramic substrates. The strength data, most relevant to canning stresses, will be presented for porous cordierite ceramic substrates as function of their contour, size and cell structure. Recent improvements in measuring the biaxial compressive strength will also be reviewed.

The stringent durability requirements approaching 100,000 vehicle miles for automotive substrates and 290,000 vehicle miles for large frontal area diesel substrates for 1994+ model year vehicles call for advanced packaging designs with thick ceramic mats and high mount densities. The latter result in high mounting pressure on the substrate and enhance its mechanical integrity against engine vibrations, road shocks and back pressure forces. A novel measurement technique which applies a uniform biaxial compressive load on the lateral surface of ceramic substrates, thereby simulating canning loads, is described. The biaxial compressive strength data obtained in this manner help determine the maximum mounting pressure and mat density for a durable packaging design. The biaxial compressive strength data for both round and non round substrates with small and large frontal area are presented.

The typical ceramic catalyst support for automotive application has a total volume of 1640 cm3. Approximately 10% of this volume is subjected to tensile thermal stresses due to a radial temperature gradient in service [1]*. These stresses are kept below 50% of the substrate strength to minimize fatigue degradation and to ensure long-term durability [2]. However, the tensile strength measurements are carried out in 4-point bending using 2.5 cm wide x 1.2 cm thick x 10 cm long modulus of rupture bars in which the specimen volume subjected to tensile stress is merely 3.2 cm3 or 0.2% of the total substrate volume [3]. Thus, a large specimen population is often necessary (50 specimens or more) to obtain the strength distribution representative of full substrate. This is particularly true for large frontal area substrates for diesel catalyst supports with an order of magnitude larger stressed volume. In this paper, the modulus of rupture data are obtained as function of specimen size.