Search Results

To reduce flow restriction of the wall flow type diesel particulate filters, the pore size distribution of DPF material was improved. Large pore material is preferred to reduce the flow restriction of the DPF. However pore diameter should be controlled within a certain limit to maintain high trapping efficiency against diesel particulates. In order to solve these conflicting matters, the mean pore diameter was enlarged from 13μm of the current material to 20 μm or more, while maintaining the cumulative volume of pores above 100μm within 8% of the total pore volume. The safe limit against thermal shock failure of the improved DPF material having 9″D x 12″/, 12.5/ volume was also determined using diesel burner regeneration system.

Ceramic wall-flow type diesel particulate filters (DPF) are being investigated for the aftertreatment systems of heavy duty engines. To use ceramic DPF more reliably and easily, electric heating regenerations are studied varying combustion air flow rates and amounts of accumulated soot. Despite electric heater capacity limitations, it is possible to regenerate DPF at a certain combustion air flow rate without thermal shock failure. The maximum withstood temperature against thermal shock failure of electric heating regeneration is similar to that of diesel burner regeneration on DPF with a nine inch diameter and a twelve inch length.

HC emission standards will be tightened during the 1990's in the US. A key issue in reducing HC emission is improving the warm-up characteristics of catalysts during the cold start of engines. For this purpose, studies are under way on reduction of heat mass of ceramic substrates. Reduction of cell walls in substrates to thickness smaller than the current thickness of 12mil or 6mil has resulted in reduced heat mass, and also reduced flow restriction of substrates. The warm-up characteristics of low bulk density catalysts are better than those of high bulk density, i.e., the warm-up characteristics of thinner wall or lower cell density catalysts are better than those of thicker wall or higher cell density catalysts. A relationship between geometric surface area and warm-up characteristics is observed.

Ceramic honeycomb wall flow diesel particulate filters (DPF) have been investigated for use in exhaust gas control of diesel vehicles. However, before they can be used, prevention of thermal shock failure during combustion regeneration is necessary. Studies were conducted on thermal shock failures on 9-inch diameter large volume DPF during regeneration by finite element analyses (FEA). These studies reveal that, within safe limits, maximum thermal stress is almost constant even at different gas flow rates and oxygen concentrations. Regeneration tests were also conducted on large volume DPF of several materials having different pore size distributions. FEA thermal stress was compared with mechanical strength of the material at safe levels.

Ceramic honeycombs have been used as automotive catalyst supports in US, Japan, Europe and other highly urbanized countries. Now, engine output is a great concern for automanufacturers, and reduction of the wall thickness of honeycomb substrates became indespensable for maintenance of gas flow restriction to a certain low level. To reduce wall thickness, material should be strong to maintain canning strength of substrates. Mechanical strength was improved with high density cordierite. However, isostatic strength of whole substrates was still insufficient with reduced thin walls for canning in spite of the material's high mecanical strength. Discussion is carried out on further possibility of improving canning performance of thin wall substrates as well as flow restriction, and warm up characteristics.

Application of ceramic honeycomb wall-flow type diesel particulate filters (DPF) to heavy duty vehicles requires a large volume filter. Heavy duty vehicles produce a large volume exhaust gas, and pressure drop in the exhaust system must be maintained to a certain level. In addition, the filters must be designed to resist fracture from thermal stresses during regeneration. This is particularly important in heavy duty vehicles because of these extended mileage requirements. These studies of the effects of DPF volume on thermal shock resistance during regeneration reveal that the maximum failure temperatures are lower as DPF volume is increased, still maintaining 950°C maximum temperature with 12 ℓ volume and 9″D × 12″L size large DPF. Some thermal stress analyses with temperature profiles and finite element analysis were conducted on four different volume DPF during regeneration.

Thermal shock failures have been considered as one of the most significant issues for wall flow type ceramic diesel particulate filters during their regeneration. This paper describes the experiments which were conducted in order to study effects of heating rates of the accumulated diesel particulate on the thermal shock failure of the filters using an NGK soot generator. The results showed favorable heating rates of the particulate in terms of the amounts of the accumulated particulate up to which the filters are safely regenerated.

In applying ceramic honeycomb wall flow type filters to the after-treatment systems of diesel particulate from engines, the melting and thermal shock failures of ceramic diesel particulate filters (DPF) have been considered as one of the most significant issues during regeneration. This paper gives the results of experiments on the effects of cell structure i.e., wall thickness and cell density, on the melting and thermal shock regeneration failure of DPF and proposes an optimized cell structure for DPF in terms of the regeneration failure and the pressure drop which is also considered to be one of the especially important issues in fuel economy for heavy duty vehicle application.