This paper describes the function and application of the preoxidation, hydrolysis and SCR catalysts individually and as a combined system for urea SCR both in model gas and engine bench tests. Using the basic system and a non-optimized urea injection strategy 45% NOx conversion was achieved in the ESC engine test. Adding a preoxidation catalyst significantly improved the NOx conversion in the low temperature region of the engine mapping. NOx conversions over 75% can be achieved in the ESC test using this improved system. With a 50% reduced SCR catalyst volume still a NOx conversion of over 65% could be achieved. Tests after 200 hours engine aging show that the activity of the system is stable.

The following paper highlights the results of a vehicle emission improvement program with emphasis on two main points: In the initial phase, various combinations of Pd and Pt-based three-way catalyst technologies were evaluated on a TLEV and a LEV calibrated vehicle in order to generate ULEV exhaust gas levels. One goal in this portion of the study was to achieve technical equivalence between a viable Pd-based technology and a newly developed Pt-based technology. A combination of the Pd- and Pt-based technologies was able to meet the ULEV and part of the ULEV II regulations in the test vehicle after a catalyst aging cycle that resembles 50,000 miles of vehicle driving. In the later phase, a mathematical algorithm based on the original TLEV and LEV vehicle data was developed in order to conduct computer modeling of the exhaust gas aftertreatment system. This algorithm described the kinetic behavior of the individual catalysts over a broad range of reaction conditions.

Engine and laboratory tests were carried out to examine the performance of NOx adsorption catalysts for gasoline lean burn engines in fresh and aged condition. The results show that fresh NOx adsorption catalysts have the potential to meet EURO III emission standards. However, to accomplish these the fuel must contain a low sulfur concentration and the engine must be tuned to optimize the efficiency of the catalyst. After engine or furnace aging upto 750°C the catalyst shows some loss of NOx adsorption efficiency. This deterioration can be offset somewhat by increasing the frequency of lean/rich switching of the engine. Temperatures higher than 750°C may cause an irreversible destruction of the NOx, storage features while the three-way activity of the catalyst remains intact or even may improve. With reference to several physicochemical investigations it is believed that the detrimental effect of catalyst aging is attributed to two different deactivation modes.