Using sand cores, the weld-able, hollow die-cast parts have been developed. For casting, the transition flow filling method is applied to reduce gas containment and to minimize damages to the core. In designing the products, the newly developed core stress prediction system by melt pressure distribution and the newly developed in-product gas containment prediction system have been applied. The hollow die-cast frame made by the new method attains a 30% increase in rigidity and 1kg reduction of weight.

In general, welding of high-pressure die casting (DC) parts has been difficult due to gases trapped in the castings. This is a result of the high-speed turbulent flow condition of the DC process. These gases are liberated during welding and produce porosity in the weld joint. The Author had found the range where an enough welding quality was obtained without great drop in castability to the middle of the laminar flow and turbulent flow. This range has been defined as the transition zone. Moreover high strength Al-Mg-Ni alloy was developed by non-heat-treatment. The Transition Flow Filling Method(TFFM) has been developed, that can not only reduce the amount of trapped gases but also is applicable to standard high pressure die casting equipment. With this method, high quality DC parts can be produced that are weldable, strong and have high toughness.