The critical particle size for a high-pressure injection system was determined. Various double-cut test dusts ranging from 0 to 5 μm to 10 to 20 μm were evaluated to determine which test dust caused the high-pressure system to fail. With the exception of the 0- to 5-μm test dust, all test dust ranges caused failure in the high-pressure injection system. Analysis of these evaluations revealed that the critical particle size, in initiating significant abrasive wear, is 6 to 7 μm. Wear curve formulas were generated for each evaluation. A formula was derived that allows the user to determine if the fuel filter effluent will cause harmful damage to the fuel system based on the number of 5-, 10-, and 15-μm particles per milliliter present. A methodology was developed to evaluate fuel filter performance as related to engine operating conditions. The abrasive methodology can evaluate online filter efficiency and associated wear in a high-pressure injection system.