Search Results

Leaf springs are used for vehicle suspension to support the load. These springs are made of flat sections of spring steel in single or in stack of multiple layers, held together in bracketed assembly. The key characteristics of leaf spring are defined as ability to distribute stresses along its length and transmit a load over the width of the chassis structures. The most common leaf spring steels are carbon steels alloyed with Cr and micro-alloyed with Ti, V and Nb. The specific thermomechanical process and alloying elements result in specific strength and fatigue properties for spring steels. The unique properties which facilitate use of spring steel in leaf spring suspensions are ability to withstand considerable twisting or bending forces without any distortion. The microstructure of these steel determines the performance and reflects the process of steel manufacturing. The performance is mainly determined by evaluating fatigue life durability.

Structural automotive components are subjected to fatigue damage under cyclic stresses and strains. The fatigue damage initiates at stress levels lower than the elastic limit of the material and results in cracks. The Initial fatigue cracks are difficult to detect, such cracks can develop rapidly and cause sudden and brittle failure in structures. Many structural automotive components are fabricated involving weld induced local conditions such as geometry of weld toe and localized tensile residual stresses. These conditions are favorable for initiation of fatigue damage at weld toe. In current work, sever plastic deformation (SPD) which is based on high frequency impact treatment using ultrasound energy was applied on weld toe of representative weld joints. The effect of SPD on weld toe geometry modification, microstructure and residual stresses were evaluated. Microscopic and X-ray diffraction techniques were used to study the effects of SPD.

A lightweight multi-material combination of steel and aluminium alloy (Al) is becoming a novel approach towards environmentally sustainable transport systems. Studies show that 10% reduction of vehicle weight results into 3-7% reduction in specific fuel consumption in IC engines and a 13.7% improvement in electric range for electric vehicles. However, dissimilar welding of Al/steel is a key challenge because of incompatible thermo-physical properties (melting point, thermal conductivity, and coefficient of thermal expansion) and low miscibility between Al and steel. The formation of brittle and hard Al-steel intermetallic compound (IMC) at the joint interface is the major concern for dissimilar welding of Al/steel. In this work, efforts are made to check the feasibility of Ni interlayer to control IMC formation at the interface of Al/steel dissimilar welded joint. Resistance spot welding is used to join low carbon steel CR01 and Al AA6061-T6 with pure Ni interlayer.

Automotive suspension system forms the basis for the design of vehicle with durability, reliability and NVH requirements. The automotive suspension systems are exposed to dynamic and static loads which in turn demands the highest integrity and performance against fatigue based metallic degradation. The growing demand for light-weighting has culminated into numerous designs of rear twist beam suspension systems. However these designs drive their design flexibility by incorporating multiple welding joints into the suspension system. Welding joints helps in designing complex automotive systems. However, these welding joints bring in weak points as welding process itself degrades parent material and introduces areas with high tensile residual stresses. These areas with tensile residual stresses are susceptible to undergo fatigue failure. Thus, there is a need to improve welding process to mitigate harmful tensile residual stresses.

Automotive suspension system forms the basis for the design of vehicle with durability, reliability, dynamics and NVH requirements. The automotive suspension systems are exposed to dynamic and static loads which in turn demands the highest integrity and performance against fatigue based metallic degradation. The current focus in automotive industry is to reduce the weight of the automotive parts and components without compromising with its static and dynamic mechanical properties. This weight reduction imparts fuel efficiency with added advantages. High-Strength Low Alloy steel (HSLA) offers optimum combination of ductility, monotonic and cyclic mechanical properties. Furthermore, welding processes offer design flexibility to achieve robust and lightweight designs with high strength steels.

Better ride and comfort, enhanced safety, reliability and durability, lower running cost as well as cost of ownership continue to be challenges for automotive OEMs. Higher fuel efficiency is considered as USP not only for lower running cost but also is hygiene factor from sustainability point of view. This has necessitated the need for Augmenting Light weighting horizon in automotive OEMs. Augmenting this leads to invention of innovative materials and processes for emerging cost competitive market. This paper focuses on technology efforts towards augmenting light weighting Horizon in Automotive. Light weighting concepts being explored by OEMs with the help of automotive component manufacturers from Powertrain - Engines & Transmission, Chassis and Suspension are discussed.