A nano-composite high strength (NCHS) steel was tested and evaluated in this work. Monotonic tension, strain controlled fatigue and fracture toughness tests were conducted at ambient temperature. Chemical composition, microstructure and fractography analysis were also performed. The NCHS steel showed excellent combination of high strength, high ductility and high fracture toughness with relatively low alloy content, compared with a S7 tool steel. Fatigue performance of the NCHS steel was also better than that of S7 tool steel. With the exceptional combination of high strength and high fracture toughness, the nano-composite high strength steel may have potential applications in gears, shafts, tools and dies where high fatigue performance, shock load resistance, wear and corrosion resistance is required.

A new proprietary Atmospheric Pressure Microwave Plasma Technology, developed for various materials processing applications, has been applied to P/M sintering of cam lobes. The aims were a) to compare the new processing route with conventional process for the same alloy composition and b) to check the possibility of successful sintering at higher temperatures so that different higher temperature P/M alloys may be used. P/M green cam lobes were used, and sintering runs were carried out initially at temperatures comparable to that currently used in the conventional processes; this was followed by runs at higher temperatures that are not very practical in the conventional processing route due to equipment component constraints. Properties such as density and hardness were measured for the sintered samples, together with corresponding microstructural analysis.

Shaft surface texture plays a very important role in rotary oil seal system performance. Functionally, the shaft surface has to prevent oil leakage via pumping between the shaft and seal. The shaft surface texture must also provide adequate contact with the seal lip, while maintaining a lubricant film. Furthermore, the initial surface texture of the shaft plays a vital role in the process of oil seal lip break-in. The shaft surface finish specification is typically Ra, 10 to 20 μ″ with a 0° ± 0.05°lead angle. The paper will describe a new surface measurement method based on interference microscopy, which generates a visual representation of a significant portion of the shaft surface texture to allow direct lead angle detection. Using this new technique, this paper will demonstrate the heredity of lead generation. The shaft 3D surface texture measurement also provides a measure of the surface volume available for lubricant retention.