Search Results

Close-coupled or manifold catalysts have been extensively employed to reduce emissions during cold start by achieving quick catalyst light-off. These catalysts must have good thermal durability, high intrinsic light-off activity and high HC/CO/NOx conversions at high temperature and flow conditions. A number of studies have been dedicated to engine control, manifold design and converter optimization to reduce cold start emissions. The current paper focuses on the effect of catalyst design parameters and their performance response to different engine operating conditions. Key design parameters such as catalyst formulation (CeO2 vs. non CeO2), precious metal loading and composition (Pd vs. Pd/Rh), washcoat loading, catalyst thermal mass, substrate properties and key application (in use) parameters such as catalyst aging, exhaust A/F ratio, A/F ratio modulation, exhaust temperature, temperature rise rate and exhaust flow rate were studied on engine dynamometers in a systematic manner.

FTP emissions from a 2.2L four cylinder vehicle are measured from six different converters. These converters have been designed to have both similar flow restriction and to have similar platinum group metals. The durability of these six converters is evaluated after dynamometer aging of both 125 and 250 hours of RATsm aging. These catalytic converters use various combinations of 400/3.5 (400 cells/in2/3.5mil wall), 400/4.5, 400/6.5, 600/3.5, 600/4.5, and 900/2.5 ceramic substrates in order to meet a restriction target and to maximize converter geometric surface area. Total catalyst volume of the converters varies from 1.9 to 0.82 liters. Catalyst frontal area varies from 68 cm2 to 88 cm2. Five of the six converters use two catalyst bricks. The front catalyst brick uses either a three-way Pd washcoat technology containing ceria or a non-ceria Pd washcoat technology. To minimize dependence on palladium the rear brick uses a Pt/Rh washcoat at a loading of 0.06 Toz and a ratio of 5/0/1.

FTP and ECE + EUDC emissions are measured from six converters having similar restriction and platinum group metals on two 1999 prototype engines/calibrations. A 2.2L four cylinder prototype vehicle is used to measure FTP emissions and an auto-driver dynamometer with a prototype 2.4L four cylinder engine is used to determine the ECE + EUDC emissions. The catalytic converters use various combinations of 400/3.5 (400cpsi/3.5mil wall), 400/4.5, 400/6.5, 600/3.5, 600/4.5, and 900/2.5 ceramic substrates in order to meet a restriction target and to maximize converter geometric surface area. Total catalyst volume of the converters varies from 1.9 to 0.82 liters. Catalyst frontal area varies from 68 cm2 to 88 cm2. Five of the six converters use two catalyst bricks. The front catalyst brick uses either a three-way Pd washcoat technology containing ceria or a non-ceria Pd washcoat technology. Pd loadings are 0.1 troy oz. of Pd.

With stricter emissions standards, low back pressure requirements, and 100,000 mile durability specifications, ceramic catalysts have undergone significant developments over the past few years. The thrust in the ceramics area has centered on thin-wall structures to minimize back pressure and on high cell density for rapid light-off in close-coupled applications. The thin-wall structures are extruded from low expansion cordierite ceramic with adequate strength and thermal shock resistance equivalent to those of standard cordierite substrate. Examples of thin-wall substrate include 350XT which is extruded from a very low expansion dense cordierite ceramic, and 400/4 and 600/4 cell structures extruded from a low expansion modified cordierite ceramic. This paper will focus on the high fatigue resistance, excellent conversion efficiency, and low back pressure of 350 XT substrates with advanced washcoat system.