In this research helical Carbon Nanotubes (CNTs) with various weight percentages as an additional reinforcement were used. The objective was to investigate the effectiveness of helical geometries of the CNTs to form interlocking mechanisms with the resin and the traditional microfiber reinforcements to improve the overall performance of the composite structures and assemblies. In this study, ASTM D2344/2344M-16 is used to study the short beam strength of the laminated nanocomposites and evaluate the benefit of the mechanically interlocked helical CNTs reinforcement. Overall, three sets of composite laminates (i.e., with neat epoxy, and with two different wt% of Helical CNTs reinforced epoxy) were fabricated per ASTM standard D2344/2344M-16. Adequate test specimens were prepared and then they were tested per ASTM standard. The test results were analyzed and evaluated to determine the effects of helical CNTs on short beam strength of the laminated nanocomposites.

Most composite assemblies and structures generally fail due to weak interlaminar properties and poor performance of their bonded joints that are assembled together with an adhesive layer. Adhesive failure and cohesive failure are among the most commonly observed failure modes in composite bonded joint assemblies. These failure modes occur due to the lack of reinforcement within the adhesive layer in transverse direction. In addition, the laminated composites fail due to the same reason that is the lack of reinforcement through the thickness direction between the laminae. The overall performance of any composite structures and assemblies largely depends on the interlaminar properties and the performance of its bonded joints. Various techniques and processes were developed in recent years to improve mechanical performance of the composite structures and assemblies, one of which includes the use of nanoscale reinforcements in between the laminae and within the adhesive layer.