Search Results

Engine oil plays an important role in improving fuel economy of vehicles by reducing frictional losses in an engine. Our previous investigation explored the friction reduction potential of next generation engine oils by looking into the effects of friction modifiers and dispersant Inhibitor packages when engine oil was fresh. However, engine oil starts aging the moment engine start firing because of high temperature and interactions with combustion gases. Therefore, it is more relevant to investigate friction characteristics of aged oils. In this investigation, oils were aged for 5000 miles in taxi cab application.

Friction reduction in lubricated components through engine oil formulations has been investigated in the present work. Three different DI packages in combination with one friction modifier were blended in SAE 5 W-20 and SAE 0 W-16 viscosity grades. The friction performance of these oils was compared with GF-5 SAE 5 W-20 oil. A motored cranktrain assembly has been used to evaluate these, in which friction mean effective pressure (FMEP) as a function of engine speeds at different lubricant temperatures is measured. Results show that the choice of DI package plays a significant role in friction reduction. Results obtained from the mini-traction machine (MTM2) provide detailed information on traction coefficient in boundary, mixed and elastohydrodynamic (EHD) lubrication regimes. It has been shown that the results from the cranktrain rig are fairly consistent with those found in MTM2 tests for all the lubricants tested.

The oil and additive industry is challenged to meet future automotive legislations aimed at reducing worldwide CO2 emissions levels. The most efficient solution used to date has been to decrease oil viscosity leading to the introduction of new SAE grades. However this solution may soon reach its limit due to potential issues related to wear with lower engine oil viscosities. In this paper, an innovative solution is proposed that combines the use of a new tailor-made polyalkylene glycol (PAG) with specific anti-wear additives. Valvetrain wear measurements using radionuclide technique demonstrates the robustness of this solution. The wear performance was also confirmed in Sequence IVA test. An extensive tribological evaluation (film formation, wear and tribofilm surface analysis) of the interactions between the base oil and the anti-wear additives lead us to propose an underlying mechanism that can explain this performance benefit.

The application of polyalkylene glycol (PAG) as a base stock for engine oil formulation has been explored for substantial fuel economy gain over traditional formulations with mineral oils. Various PAG chemistries were explored depending on feed stock material used for manufacturing. All formulations except one have the same additive package. The friction performance of these oils was evaluated in a motored single cylinder engine with current production engine hardware in the temperature range 40°C-120°C and in the speed range of 500 RPM-2500 RPM. PAG formulations showed up to 50% friction reduction over GF-5 SAE 5W-20 oil depending on temperature, speed, and oil chemistry. Friction evaluation in a motored I-4 engine showed up to 11% friction reduction in the temperature range 40°C-100°C over GF-5 oil. The paper will share results on ASTM Sequence VID fuel economy, Sequence IVA wear, and Sequence VG sludge and varnish tests. Chassis roll fuel economy data will also be shared.