Corrosion stiction at the contact interface between a brake friction material and a gray iron disc under the parking brake condition was investigated by evaluating the possible parameters that affect the shear force to detach the corroded interface. Using production brake friction materials, comprising non-steel and low-steel types, corrosion tests were carried out by pressing the brake pad onto the gray iron disc using a clamp at various conditions. Results showed that the shear force to detach the corroded interface tended to increase with applied pressure and corrosion time. On the other hand, porosity, acidity, and hydrophobicity of the friction material did not show a reliable correlation to the stiction force. The poor correlation of the stiction force with the friction material properties indicated that the stiction force was not determined by a single factor but governed by multiple parameters including surface contact areas and inhomogeneity of the ingredients.

It is widely believed or speculated that higher pad compressibility leads to reduced brake squeal and that caliper design can affect brake squeal. After encountering anecdotal contradictory cases, this investigation was undertaken to systematically generate basic data and clarify the beliefs or speculations. In order to adjust pad compressibility, it is common to modify pad molding temperatures, pressures and times, which in addition to changing the compressibility, changes friction coefficient and physical properties of the pad at the same time. In order to separate these two effects, NAO disc pads were prepared under the same molding conditions while using different thicknesses of the underlayer to achieve different compressibilities, thus changing the compressibility only without changing the friction coefficient and physical properties of the pad.

When two identical brakes are simultaneously tested on a vehicle chassis dynamometer, very often the left hand brake is found to squeal more or less than the right hand brake, all at different frequencies. This study was performed to develop some understanding of this puzzling phenomenon. It is found that as the wear rate difference between the inner pad and the outer pad increases, low frequency (caliper and knuckle) squeals occur more and more, and as the differential wear becomes larger and larger, high frequency (disc) squeals occur less and less, finally disappearing all together. Discs and calipers are found to affect the differential pad wear, in turn affecting brake squeal generation.