This work consists of evaluating the influence of heat treatment on sintered valve seat insert (VSI) obtained with two different high-speed steels powders and one tool steel: AISI M3:2, AISI M2 and AISI D2, respectively. The high-speed / tool steel powders were mixed with iron powders and additives such as manganese sulphide, zinc stearate, graphite and niobium carbide. All the high-speed / tool steel powders had its particle size distribution and morphology analyzed. The heat treatment of the VSI consisted of air quenching followed by double tempering it in seven different and equidistant temperatures, ranging from 100 °C until 700 °C. A data acquisition system with a thermocouple type k attached to the samples was used to determine the air-quenching cooling rate. The mechanical and physical properties measurements were carried out, i.e., apparent density, apparent hardness and crush radial strength.

This paper reports the experimental efforts in recording the 2-dimensional temperature distribution on autogenous thin plates of UNS S32304 steel during welding. The butt-welded autogenous joints were experimentally performed by the GTAW (Gas Tungsten Arc Welding) process with either argon or argon-2%nitrogen atmospheres. The temperatures cycles were recorded by means of thermocouples embedded by spot welding on the plate's surfaces and connected to a multi-channel data acquisition system. The laser flash method (LFM) was also used for the determination thermal diffusivity of the material in the thickness direction. The temperature curves suggest a relationship between the microstructures in the solidified and the heat affected zone with the diffusivity variation. This is a region where there had been a major incidence of heat. The obtained results validate the reliability of the experimental used apparatus.