Zinc-coatings with a substantial Magnesium content have been in use for over 30 years by now. Unlike the well-established Zn-Al-Mg coatings originating from Japan which have significant higher alloying contents applied mainly for building applications, this Zinc Magnesium Aluminum coating (ZM) is also specifically designed to meet the requirements of car manufacturers. The ZM coating introduced by voestalpine, corrender, is in the upper range of ZM-alloying compositions, which was set by VDA (German Association of the Automotive Industry) and SAE to be within 1.0 to 2.0 wt. % Mg and 1.0 to 3.0 wt. % Al. The properties of these “European” Zinc-Magnesium coatings are well comparable within this range. Compared to GI and GA ZM coatings exhibit significant advantages in the press shops with its excellent formability and reduced galling and powdering respectively which is a significant advantage for the forming of outer panels.

Press-hardening steels get more and more popular for body in white applications as an approach to meet the demands of passenger safety and CO2 reduction. Unlike the larger part of the structure that is typically zinc coated, the majority of the PHS parts is either uncoated or aluminum silicon coated. This paper shall give an overview of press-hardening steels with zinc coatings with detailed results for corrosion resistance, weldability and mechanical properties for strength levels of 490 to 1800 MPa. Furthermore as for zinc coated material maintaining a robust press-hardening process is of even higher importance than for uncoated or AlSi coated material. A range of different processes including indirect and direct process are shown in detail. Especially the topic of micro-cracks, mechanisms and avoidance of micro-cracks in the direct process will be discussed. Results from industrial and semi industrial production are shown.