Stamping die design recommendations attempt to limit the production of burrs through accurate alignment of the upper and lower trimming edges. For aluminum automotive exterior panels, this translates to a clearance less than 0.1 mm. However, quality of sheared edge and its stretchability are affected by stiffness of the cutting tool against opening of the clearance between the shearing edges. The objective of the study is to investigate the influence of stiffness of trimming or piercing dies against opening of the cutting clearance on sheared edge stretchability of aluminum blanks 6111-T4. For experimental study, one side of the sample had sheared surface obtained by the trimming process while the other side of the sample had a smooth surface achieved by metal finish. Burr heights of the sheared edge after different trimming configurations with 10% clearance were measured.

Experimental results on influence of trimming conditions on the shape of the sheared surface are combined with the results of stretching sheared samples after trimming. The objective of the research described in this paper is to study the mechanism of fracture initiation and cracks propagation during half-a-dog bone tensile test representing sheared edge stretching condition. One side of the sample had sheared surface obtained by the trimming process while the other side of the sample had a smooth surface. Significant attention was paid to understanding of fracture sources. An interrupted tensile test approach was employed to track fracture initiation and propagation during stretching of sheared surface. The results of the experimental study indicated that multiple sources of fracture were observed in the burr area for trimming with clearances exceeding 10% of the material thickness.

Experimental results on influence of trimming conditions on the shape of the sheared surface are combined with the results of stretching sheared samples after trimming. The objective of the research described in this paper is to study the mechanism of fracture initiation and cracks propagation during half-a-dog bone tensile test representing sheared edge stretching condition. One side of the sample had sheared surface obtained by the trimming process while the other side of the sample had a smooth surface. Significant attention was paid to understanding of fracture sources. An interrupted tensile test approach was employed to track fracture initiation and propagation during stretching of sheared surface. The results of the experimental study indicated that multiple sources of fracture were observed in the burr area for trimming with clearances exceeding 10% of the material thickness.