The objective of this study was to investigate which of the artificial aging cycles available in the automotive industry that causes major deactivation of three-way catalysts (TWCs) and can be used to obtain an aged catalyst similar to the road aged converter (160 000km). Standard bench cycle (SBC) aging with secondary air injection (SAI) covered aging with various mass flows - a flow from three cylinders into one catalyst system and a flow from three cylinders into two parallel connected catalysts. For rapid catalyst bench aging, secondary air injection is a very efficient tool to create exotherms. Furthermore, the effect on catalytic activity of SAI aging with poisons from oil and fuel dopants (P, Ca, Zn) was investigated. The catalysts were thoroughly characterized in light-off and oxygen storage capacity measurements, emission conversion as a function of lambda and load variation was determined.

The effect of various fuel-cut agings, on a Volvo Cars 4-cylinder gasoline engine, with bimetallic three-way catalysts (TWCs) was examined. Deactivation during retardation fuel-cut (low load) and acceleration fuel-cut (high load, e.g. gearshift or traction control) was compared to aging at λ=1. Three-way catalysts were aged on an engine bench comparing two fuel-cut strategies and their impact on of the life and performance of the catalysts. In greater detail, the catalytic activity, stability and selectivity were studied. Furthermore, the catalysts were thoroughly analyzed using light-off and oxygen storage capacity measurements. The emission conversion as a function of various lambda values and loads was also determined. Fresh and 40-hour aged samples showed that the acceleration fuel-cut was the strategy that had the highest contribution towards the total deactivation of the catalyst system.