Search Results

Weld lines can significantly reduce ultimate tensile strength (UTS) and fracture strain of talc filled polypropylene (PP). In this paper, two different injection molding tests were completed. First, an injection mold with triangular inserts was built to study the influence of meeting angles on material properties at the weld line region. Tensile samples were cut at different locations along the weld line on the injection molded plaques. The test results showed that both UTS and fracture strain increase when the sample locations are away from the insert. This trend is attributed to different meeting angles. Second, standard ISO tensile bars with and without weld line were injection molded to identify the size of the weld line affected zone. A FEA model was built in ABAQUS, where the tensile sample was divided into two different regions, the solid region and the weld line affected region.

Weld lines occur when melt flow fronts meet during the injection molding of plastic parts. It is important to investigate the weld line because the weld line area can induce potential failure of structural application. In this paper, a weld line factor (W-L factor) was adopted to describe the strength reduction to the ultimate strength due to the appearance of weld line. There were two engineering thermoplastics involved in this study, including one neat PP and one of talc filled PP plastics. The experimental design was used to investigate four main injection molding parameters (melt temperature, mold temperature, injection speed and packing pressure). Both the tensile bar samples with/without weld lines were molded at each process settings. The sample strength was obtained by the tensile tests under two levels of testing speed (5mm/min and 200mm/min) and testing temperatures (room temperature and -30°C). The results showed that different materials had various values of W-L factor.

Traditionally, Knee Air Bag (KAB) is constructed of a woven nylon or polyester fabric. Recently, Ford developed an injection molded air bag system for the passenger side called Active Glove Box (AGB). This system integrates a plastic bladder welded between the glove box outer and inner doors. This new system is smaller and lighter, thus improving the roominess and other creature comforts inside the passenger cabin while providing equivalent restraint performance as traditional knee airbag system. This patented technology allows positioning of airbags in new locations within the vehicle, thus giving more freedom to designers. The first application of this technology was standard equipment on the 2015 Ford Mustang. Given that this technology is first in the industry, it was a challenge to design, test and evaluate the performance of the system as there is no benchmark to compare this technology. A CAE driven design methodology was chosen to overcome this challenge.

Injection molding tools are expensive and the fatigue failure during production would result in very costly rework on the tool and downtime. Currently, mold designs are mostly based on expert experience without a careful stress analysis and the mold tool life cycle relies largely on rough estimates. The industry state of the art applies averaged temperature change and peak pressure load on the mold tool. The static analysis is then performed. Mold temperature history and thermal shock are not considered in the durability analysis. In this paper, a transient thermal analysis of the tool is performed in conjunction with the injection molding process simulation. The spatial and temporal variation of temperature, pressure and clamping forces are exported from Moldflow simulation. These histories of temperature and pressure are converted to appropriate loading curves and mapped into Abaqus FEA model.

Long fiber reinforced plastics (LFRP) have exhibited superior mechanical performance and outstanding design flexibility, bringing them with increasing popularity in the automotive structural design. Due to the injection molding process, the distribution of long fibers varies at different locations throughout the part, resulting in anisotropic and non-uniform mechanical properties of the final LFRP parts. Images from X-ray CT scan of the materials show that local volume fraction of the long fibers tends to be higher at core than at skin layer. Also fibers are bundled and tangled to form clusters. Most of the current micromechanical material models used for LFRP are extended from those for short fibers without adequate validation. The effect of the complexity of long fibers on the material properties is not appropriately considered. Thus, modeling of these materials is lagging behind the material manufacturing and design development, which in turn limits their further development.

A CAE simulation methodology was developed to predict the warpage and shape deviation from nominal in finished plastic sub-assemblies that are joined using Infra-Red (IR), hot-plate or vibration welding processes. An automotive glove box bin and door sub-assembly was used to develop the methodology. It was seen that part warpage from injection molding and welding causes warpage in final assembled product which results in gaps and the consequent loss in quality of appearance. The CAE simulation methodology included prediction of the part warpage with residual stress from the injection molding process, use the post-molded shape as an initial part condition for the welding process, and simulation of the welding process itself.