A V-engine high pressure fuel pipe have experienced several failures during dyno engine validations at brazed joints due to combination of static and dynamic engine loads. The braze fillet experience high local stress concentration with large gradients and it was critical to capture strain contour at this spot to properly understand the failure. Strain gauges was used to measure strain but was incapable of capturing the braze fillet due to the small fillet radius and lack of real estate to install the gauge (braze fillet radius ~ 0.10 mm). A whole field optical experiment method Digital Image Correlation was utilized to successfully captured strain contour at area of interest and results fed back to computational model.

Draw beads are widely used in the binder of a draw die for regulating the restraining force and control the draw-in of a metal blank. Different sheet materials and local panel geometry request different local draw bead configurations. Even the majority of draw bead is single draw bead, the alternative double draw bead does have its advantages, such as less bending damage may be brought to the sheet material and more bead geometry features available to work on. In this paper, to measure the pulling force when a piece of sheet metal passing through a draw bead on an inclined binder, the AA5XXX and AA6XXX materials were tested and its strain were measured with a digital image correlation (DIC) system. Five different types of double bead configurations were tested. The beads are installed in a Stretch-Bend-Draw-System (SBDS) test device. The clearance between a male and a female bead is 10% thicker than the sheet material. A tensile machine was used to record the pulling force.

Bendability is one of the most important formability characteristics in sheet metal forming, so it has to be understood for robust aluminum stamping process designs. Crack is one of the major failure modes in aluminum sheet bending. In this study, a new “incremental bending” method is proposed to reduce the risk of bending failure. A novel laboratory test methodology is conducted to test the 5xxx series aluminum sheet bendability with 3D digital image correlation (DIC) measurement system. The designs of test apparatus and test procedure are introduced in this paper. Through the data processing and evaluation of a sequence image acquisition, the major strain histories within the zone of the through thickness crack of test samples are measured. Testing results show that incremental bending is capable of reducing peak strain on the outer surface obviously compared with traditional non-incremental bending. The more step, more movement, the more peak strain reduction.

Vehicle weight reduction is a significant challenge for the modern automotive industry. In recent years, the amount of vehicular components constructed from aluminum alloy has increased due to its light weighting capabilities. Automotive manufacturing processes, predominantly those utilizing various stamping applications, require a thorough understanding of aluminum fracture predictions methods, in order to accurately simulate the process using Finite Element Method (FEM) software or use it in automotive engineering manufacture. This paper presents the strain distribution of A5182 aluminum samples after punch impact under various conditions by Digital Image Correlation (DIC) system, its software also measured the complete strain history, in addition to sample curvature after it was impacted; therefore obtaining the data required to determine the amount of side-wall-curl (Aluminum sheet springback) present after formation.

In Aluminum Alloy, AA, sheet metal forming, the through thickness cracking at the edge of cut out is one of the major fracture modes. In order to prevent the edge cracking in production forming process, practical edge stretch limit criteria are needed for virtual forming prediction and early stamping trial evaluations. This paper proposes new methods for determining the edge stretching limit of the sheet coupons, with and without pre-stretching, based on the Digital Image Correlation (DIC) technique. A numbers of sets of notch-shaped smaller coupons with three different pre-stretching conditions (near 5%, 10% and fractured) are cut from the prestretched large specimens. Then the notch-shaped smaller coupons are stretched by uniaxial tension up to through edge cracking observed. A dual-camera 3D-DIC system is utilized to measure both coupon face strain and thickness strain in the notch area at the same time.

Dimensional problems for punched holes on a sheet metal stamping part include being undersized and oversized. Some important relationships among tools and products, such as the effect of conical punch tip angle, are not fully understood. To study this effect, sheets of AA6016 aluminum and BH210 steel were punched by punches with different conical tip angles. The test method and test results are presented. The piercing force and withdrawing force when using conical punches were also studied. The results indicate that the oversize issue for a punched hole in a stamped panel is largely due to the combination of the conical tip effect and the stretching-release effect.

Material formability is a very important aspect in the automotive stamping, which must be tested for the success of manufacturing. One of the most important sheet metal formability parameters for the stamping is the edge tear-ability. In this paper, a novel test method has been present to test the aluminum sheet edge tear-ability with 3D digital image correlation (DIC) system. The newly developed test specimen and fixture design are also presented. In order to capture the edge deformation and strain, sample's edge surface has been sprayed with artificial speckle. A standard MTS tensile machine was used to record the tearing load and displacement. Through the data processing and evaluation of sequence image, testing results are found valid and reliable. The results show that the 3D DIC system with double CCD can effectively carry out sheet edge tear deformation. The edge tearing test method is found to be a simple, reliable, high precision, and able to provide useful results.

This paper introduces an industrial application of digital image correlation technique on the measurement of aluminum edge stretching limit. In this study, notch-shape aluminum coupons with three different pre-strain conditions are tested. The edge stretching is proceeded by standard MTS machine. A dual-camera 3D Digital Image Correlation (DIC) system is used for the full field measurement of strain distribution in the thickness direction. Selected air brush is utilized to form a random distributed speckle pattern on the edge of sheet metal. A pair of special optical lens systems are used to observe the small measurement edge area. From the test results, it demonstrate that refer to the notched coupon thickness, pre-tension does not affect the fracture limit; refer to the virgin sheet thickness, the average edge stretch thinning limits show a consistent increasing trend as the pre-stretch strain increased.

Measuring deformation under dynamic loading is still a key problem in the automobile industry. The first spatial phase-shift shearography system for relative deformation measurement is reported. Traditional temporal phase-shift technique-based shearography systems are capable of measuring relative deformation by using a reference object. However, due to its low acquisition rate, the existing temporal phase-shift shearography system can be only used under static loading situations. This paper introduces a digital shearography system which utilizes the spatial phase-shift technique to obtain an extremely high acquisition rate. The newly developed spatial phase-shift shearography system uses a Michelson-Interferometer as the shearing device. A high power laser at 532nm wavelength is used as the light source. A one mega pixels high speed CCD camera is used to record the speckle pattern interference.

With the rapid development of computing technology, high-speed photography system and image processing recently, in order to meet growing dynamic mechanical engineering problems demand, a brief description of advances in recent research which solved some key problems of dynamic photo-elastic method will be given, including:(1) New digital dynamic photo-elastic instrument was developed. Multi-spark discharge light source was replaced by laser light source which was a high intensity light source continuous and real-time. Multiple cameras shooting system was replaced by high-speed photography system. The whole system device was controlled by software. The image optimization collection was realized and a strong guarantee was provided for digital image processing. (2)The static and dynamic photo-elastic materials were explored. The new formula and process of the dynamic photo-elastic model materials will be introduced. The silicon rubber mold was used without the release agent.

The port structure consisting of spur pile, vertical pile and beam is subjected to impact loads, so its internal stress state of each point will rapidly change over time. Dynamic photoelastic method is used to study the dynamic stress and stress wave propagation. With epoxy resin and other materials, a photoelastic model of beam to column connection structure is processed and product. The dynamic response of the model under the impact load by the free fall is researched by the dynamic photoelastic method, and recorded by the new digital dynamic photoelastic system with a laser source and high-speed photography system. The internal dynamic stress propagation and distribution, the maximum shear stress and the dynamic stress concentration problems can be obtained by analyzing the dynamic response.

In this paper, Digital Image Correlation Method (DICM) is employed to measure the shear mechanical property of the new style automotive structural adhesive specimens and traditional spot welded specimens under quasi static uniaxial shear tensile test. This experiment adopts a non-contact measuring method to measure the strain of specimens. A CCD and a computer image processing system are used to capture and record the real-time surface images of the specimens before and after deformation. Digital correlation software is used to process the imagines before and after deformation to obtain the specimen's strain of the moment. And then both the force-displacement curve and the stress-strain curve during the tensile process could be obtained. The test and analysis results show that the new style structural adhesive specimens have a great advantage with the spot welded specimens. It provides experimental evidence for further improvement of this structural adhesive.

When an object was subjected an impact loading, stress wave was produced in the object. Studying the regularity of stress-wave propagation was significant to the study of objects subjected to impact loading. When stress wave travelled in the object, principal stress on free boundary was useful to theoretical analysis and calculation. In this article, a new kind of dynamic photoelastic apparatus was used. Isochromatic and isoclinic of the object subjected to impact loading could be obtained combining dynamic photoelastic experiment and related test equipment. By analyzing the isoclinic, there would be a conclusion that the angle between the isoclinic and the free boundary was not 0°or 90°. So the values of the two principal stress on the boundary were all not 0. The result obtained from the electrometric method came to the same conclusion. Analysis showed the result of dynamic photoelastic method was compatible with the result of electrometric method.