This article delineates the importance of infrastructure and its related aspects on sustainability of transportation on global and local context. Almost 7% of the GDP in India is spent on transportation and 6% of the CO2 emissions in the world is due to transportation. In countries like India, the road transport has significantly grown over other forms of mobility. This articles introduces different forms of transportations that exists today and the importance of sustainability in transportation sector. Sustainable transportation depends on development of infrastructure to enable smart transport solutions involving intelligent transport system, electric mobility, information management, vehicle health monitoring, advanced traffic management system and driver assistance system in a vehicle. The challenges includes existing transport operations, environmental impact and complexity of existing transport network.

Mechanical and wear properties of Al alloyed gray cast iron (0.5% and 1.0%) were compared with that of Mo (1.0%) and Cu (0.77%) alloyed gray cast iron in this investigation. All the alloys showed pearlitic microstructure. The graphite morphology varied due to varying chemistry. The fracture surface showed “cabbage” like dimpled morphology indicating the predominant ductile fracture. It was found that the Mo containing cast iron show 25 to 30% higher strength and 6 to 7 times better wear resistance compared to Al containing cast irons. The worn surface showed oxide formation during sliding.

The strength and wear resistance of four alloyed cast irons with elements like Ni. Mo, Cu, Cr and Al have been compared and analyzed. The increased hardness is reducing the wear resistance of the alloy due to graphite flakes. Higher carbon produces more graphite flakes which act as weak points for reducing strength and wear resistance. The wear rate increases for harder cast iron sample with more graphite flakes. Wear rate drastically increases with increase in carbon equivalent. Strength was found to decrease for samples with higher graphite flakes. The wear debris consisted of graphite flakes in platelet like morphology along with iron particles from the matrix. The presence of carbon at the sliding interface also sometimes decreases wear rate.