Heat exchangers used as charge air coolers are repeatedly subjected to thermal strain, which may cause fracture. To predict the durability of heat exchangers, stress estimations using Finite Element Analysis (FEA) are effective. However, producing a detailed finite element model would require an enormous number of elements and excessive calculation costs. To resolve this problem, we focused on periodic tube-fin structures, considering actual and designed fin shapes, and applied a homogenization method to the fins. We then determined their homogenization elastic stiffness and verified it by conducting compression experiments and analyses using partial models consisting of laminated tube-fin structures. If fins are homogenized, it is important that homogenization be based on the actual fin shape. We then produced a finite element model of a charge air cooler assembly by using the homogenization element, and conducted analyses which simulated a thermal fatigue test.

Measurements of residual stress in a printed circuit board, which consists of copper foil, silver alloy and thermo plastic resin, were conducted under a thermal cycle. The printed circuit board was given a ten-layer repeat of prepreg and made by thermocompression bonding. Experiments suggested the possibility of measuring surface residual stress of copper circuits and the internal residual stress of metallic connections by synchrotron radiation of Spring-8. FEM analysis of the printed circuit board during a thermal cycle was conducted, and the result was adjusted to X-ray stress using absorption correction. X-ray stress during a heat-cycle obtained by synchrotron radiation showed good agreement with stress calculated by FEM analysis.

To meet diesel emission regulations, high injection pressure is demanded for the supply pump of electronically controlled common-rail type injection system. DENSO has produced common-rail type injection system in 1999. Cam and roller to generate high pressure in the supply pump at the system are composed of steel and silicon nitride ceramics, and are rolling contact under light oil lubrication. Therefore, rolling contact fatigue failure had been concerned. In order to assure the components, we estimated the influence on the materials and the lubrication on the rolling fatigue strength of silicon nitride ceramics, the contact fatigue life was tested under oil lubrication.