Tribological performance of tungsten sulfide (WS2) nanoparticles, microparticles and mixtures of the two were investigated. Previous research showed that friction and wear reduction can be achieved with nanoparticles. Often these improvements were mutually exclusive, or achieved under special conditions (high temperature, high vacuum) or with hard-to-synthesize inorganic-fullerene WS2 nanoparticles. This study aimed at investigating the friction and wear reduction of WS2 of nanoparticles and microparticles that can be synthesized in bulk and/or purchased off the shelf. Mixtures of WS2 nanoparticles and microparticles were also tested to see if a combination of reduced friction and wear would be achieved. The effect of the mixing process on the morphology of the particles was also reported. The microparticles showed the largest reduction in coefficient of friction while the nanoparticles showed the largest wear scar area reduction.

The tribological performance of nanofluids consisting of ZnO nanoparticles dispersed with a stabilizer in an API Group III oil was investigated. Recent research suggests that these fluids may reduce friction and wear compared to the base oil when used as a lubricant in metal-on-metal tests. The effects of nanoparticle concentration and test temperature on friction and wear were studied. Tests were run at 50°C and 100°C to investigate the viability of the fluids at elevated temperatures because possible applications include use as engine lubricants. Nanofluids showed friction reduction of up to 5.2% and reduced wear by up to 82.8% versus oil with only stabilizer at the highest ZnO concentration and the lowest temperature. Stabilizer increased wear at every concentration, but did not affect friction significantly. Fluid viscosity was also investigated. At 30°C, significant shear-thinning behavior was observed for the 2% ZnO solution, and a viscosity versus shear rate curve was found.