1 One issue raised by the use of austenitic stainless steels in commercial vehicles is the increase in material costs. To reduce those material costs, a nitric acid electropolishing treatment was applied to SUS436L (18 Cr - 1.5 Mo - 0.4 Nb) and corrosion tests were conducted to compare its corrosion resistance to that of SUS316L(16 Cr - 12 Ni - 2 Mo). Compared to SUS316L, SUS436L subjected to nitric acid electropolishing indicated superior corrosion resistance. In addition, XPS and TEM analyses showed that while the SUS436L passivation film layer contained approximately twice as much chromium, its thickness was also generally reduced by approximately half, to 2 nm. These results suggest that electropolishing with nitric acid, which is highly oxidative, formed a fine passivation film.

The friction pattern on the chamfers of sleeves and dog gears is a combination of peeling and adhesive wear caused by the formation and propagation of fine cracks. The effect of additional elements on wear were checked by making a test apparatus capable of performing evaluations on test pieces equivalent to those using actual parts. The results showed that the addition of B, Ti-Nb helped improve wear resistance. This is attributed to enhanced toughness and reduced peeling due to the formation of a texture. A 45% reduction in wear was achieved in actual parts tests on steel with added B, Ti-Nb.

Wear resistance is the important characteristics of cast iron materials for automobile components. Because the phenomenon of wear is a highly complicated mechanism involving many factors such as surface conditions, chemical reactions with lubricants, metals, and physics, it has not been fully explained. Therefore, it will be necessary to confirm and explain the wear mechanism to develop effective improvements. The purpose of this study was to investigate the structural change behavior and effects of alloying elements when the material top surface becomes worn, in order to improve the wear resistance of cylinder liners and other cast iron materials. For this purpose, several types of prototype materials were produced, and the relationship between components and wear resistance was investigated by using a laser microscope for quantitative observation of the degree of pearlite microstructure fineness.

We have developed a new test method in which temperature of cavity lip of a piston alone during engine rotation is reproduced, cavity lip strain is measured. As the results of strain measurement using the test method in a condition that simulates of conventional engines, a strain behavior was out-of-phase. And in a condition that simulates of high-load engines in future, strain behavior was clockwise-diamond cycle. It was found from the result of the test method developed that strain increased on the cavity lip. The fatigue life of the cavity lip was evaluated using the strain measured and isothermal fatigue curves which obtained by the strain controlled isothermal fatigue test. The result of engine durability test has revealed that the developed method was valid for thermal fatigue evaluation of the cavity lip.