In this paper, failure modes of dissimilar laser welds in lap-shear specimens of low carbon steel and high strength low alloy (HSLA) steel sheets are investigated based on experimental observations. Micro-hardness tests across the weld zones of dissimilar laser welds were conducted. The hardness values of the fusion zones and heat affected zones are significantly higher than those of the base metals. The fatigue lives and the corresponding failure modes of laser welds as functions of the load ranges are then examined. Optical micrographs of the laser welds before and after failure under quasi-static and cyclic loading conditions are then examined. The failure modes and fatigue behaviors of the laser welds under different loading conditions are different. Under quasi-static loading conditions, a necking failure occurred in the upper low carbon steel sheet far away from the laser weld.

Fatigue behavior of self-piercing rivets (SPRs) and clinch joints in lap-shear specimens of 6111-T4 aluminum sheets is investigated based on experimental observations and a fatigue life estimation model. Lap-shear specimens with SRPs and clinch joints were tested under cyclic loading conditions. Under cyclic loading conditions, fatigue cracks start from the curved interfacial surface of the upper sheet and then grow into the upper sheet thickness for both self-piercing rivets and clinch joints. The self-piercing rivets and clinch joints fail finally through the circumferential/transverse crack growth in the upper sheets and inner button crack growth, respectively. The structural stress solution and the experimental stress-life data for aluminum 6111-T4 sheets are adopted to estimate the fatigue lives of both types of joints. The fatigue life estimations based on the structural stress model show good agreement with the experimental results.