Fretting is an important phenomenon that happens in many mechanical parts. It is the main reason in deadly failures in automobiles, airliners, and turbine engines. The damage is noticed between two surfaces clamped together by bolts or rivets that are nominally at rest, but have a small amplitude oscillation because of vibration or local cyclic loading. Fretting damage can be divided into two types. The first type is the fretting fatigue damage where a crack would initiate and propagate at specific location at the interface of the mating surfaces. Cracks usually initiate in the material with lower strength because of the local cyclic loading conditions which eventually lead to full failure. The second type is the fretting wear damage because of external vibration. Researchers have investigated this phenomenon by theoretical modeling and experimental approaches. Although a lot of research has been done on fretting damage, some of the parameters have not been well studied.

Two popular critical plane models developed by Fatemi-Socie and Smith-Watson-Topper were derived from the experimental observations of the nucleation and growth of cracks during loading. The Fatemi-Socie critical plane model is applicable for the life prediction of materials for which the dominant failure mechanism is shear crack nucleation and growth, while the Smith-Watson-Topper model, for materials that fail predominantly by crack growth on planes perpendicular to the planes of maximum tensile strain or stress. The two critical plane models have been validated primarily by in-phase and 90° out-of-phase loading, and few, on the complex, non-proportional loading paths. A successful critical plane model should be able to predict both the fatigue life and the dominant failure planes. However, some experimental studies indicate the 304 stainless steel has the two possible failure modes, shear and tensile failure dominant, depending on the loading mode and stress and strain states.

One of the major problems that the automotive industry faces is reducing friction to increase efficiency. Researchers have shown that 30% of the fuel energy was consumed to overcome the friction forces between the moving parts of any automobile, Holmberg et al. [1]. The interface of the piston pin and pin bore is one of the areas that generate high friction under severe working conditions of high temperature and lack of lubrication. In this research, experimental investigation and theoretical simulation have been carried out to analyze the motion of the floating pin against pin bore. In the experimental study, the focus was on analyzing the floating pin motion by using a bench test rig to simulate the floating pin motion in an internal combustion engine. A motion data acquisition system was developed to capture and record the pin motion. Thousands of images were recorded and later analyzed by a code written by MATLAB.