Three established mechanical test specimen geometries and test methods used to evaluate mechanical properties of brittle materials are adapted to the diesel particulate filter (DPF) architecture to evaluate failure initiation stress and apparent elastic modulus of the ceramics comprising DPFs. The three custom-designed test coupons are harvested out of DPFs to promote a particular combination of orientation of crack initiation and crack plane. The testing of the DPF biaxial flexure disk produces a radial tensile stress and a crack plane parallel with the DPF's longitudinal axis. The testing of the DPF sectored flexural specimen produces axial tension at the DPF's OD and a crack plane perpendicular to the DPF's longitudinal axis. The testing of the DPF o-ring specimen produces hoop tension at the DPF's original outer diameter (OD) and at the inner diameter of the test coupon, and a crack plane parallel to the DPF's longitudinal axis.

Alkali and alkaline earth metal impurities found in diesel fuels are potential poisons for diesel exhaust catalysts. Using an accelerated aging procedure, a set of production exhaust systems from a 2011 Ford F250 equipped with a 6.7L diesel engine have been aged to an equivalent of 150,000 miles of thermal aging and metal exposure. These exhaust systems included a diesel oxidation catalyst (DOC), selective catalytic reduction (SCR) catalyst, and diesel particulate filter (DPF). Four separate exhaust systems were aged, each with a different fuel: ULSD containing no measureable metals, B20 containing sodium, B20 containing potassium and B20 containing calcium. Metals levels were selected to simulate the maximum allowable levels in B100 according to the ASTM D6751 standard. Analysis of the aged catalysts included Federal Test Procedure emissions testing with the systems installed on a Ford F250 pickup, bench flow reactor testing of catalyst cores, and electron probe microanalysis (EPMA).