Search Results

The diesel particulate membrane filter (DPMF) is a good solution to the problem of high pressure drop that exists across diesel particulate filters (DPFs) as a result of the soot trapping process. Moreover, DPMFs that have a membrane layer composed of SiC nanoparticles can reduce the oxidation temperature of soot and the apparent activation energy. The SiC nanoparticles have an oxide layer on their surface, with a thickness less than 10 nm. From the visualization of soot oxidation on the surface of SiC nanoparticles by an environmental transmission electron microscope (ETEM), soot oxidation is seen to occur at the interface between the soot and oxide layers. The soot oxidation temperature dependency of the contact area between soot and SiC nanoparticles was evaluated using a temperature programmed reactor (TPR). The contact area between soot and SiC nanoparticles was varied by changing the ratio of SiC nanoparticles and carbon black (CB), which was used as an alternative to soot.

A diesel particulate membrane filter (DPMF) offers good trapping efficiency of soot and reduces the pressure loss through the soot-trapping process. We found that one specific design of DPMF has the effect of reducing the apparent activation energy of the soot oxidation. The membrane is made of SiC nanoparticles with a diameter of 10-100 nm, which are covered with a thin silicon-oxy-carbide layer with a thickness of about 5 nm. The apparent activation energy of soot oxidation on the DPMF was reduced by 30-40 kJ/mol than conventional SiC-DPF. Furthermore, the light-off temperature of soot oxidation on the DPMF (with single nanosized Pt) is about 100°C lower than that of the DPMF (without Pt). The single nanosized Pt particles are embedded in the silicon-oxy-carbide layer. The formation of additional Pt is different from that which takes place in a conventional catalyzed soot filter (CSF). In a conventional CSF, the surface of the Pt particles is exposed to the atmosphere.

A diesel particulate membrane filter (DPMF) has good trapping efficiency of soot and reduces the pressure loss through the soot accumulation process on the diesel particulate filter wall. The activation energy reduction effect of the soot oxidation reaction by DPMF was clarified. The membrane consists of SiC nanoparticles with a diameter of 10-100 nm. A thin oxide layer is formed on the SiC particle surface, and nanoscale noble metal particles are distributed on the surface. The reduction mechanism for the activation energy was investigated in detail. Nanoscale soot was accumulated on DPMF from a diesel lamp. Furthermore, the soot oxidation in the regeneration process was observed using an optical microscope. An Arrhenius plot was made from the change of the concentration of the product gases CO and CO₂ with respect to time. The performance and the temperature dependence of oxygen desorption on the oxide layer was measured by thermal desorption spectroscopy (TDS).

A highly robust Diesel Oxidation Catalyst (DOC) for use with a dual mode combustion system, which makes it possible to switch the combustion between conventional mode and PCI (Premixed Compression Ignition) Combustion mode, was studied. Firstly, commercially available DOCs were tested to confirm current level of emission reduction efficiency for a simulated dual mode combustion system, where CO (Carbon monoxide) was varied from 500 to 5,000 ppm, HC (Hydrocarbon) was varied from 500 to 5,000 ppmC and O2 (Oxygen) was varied from 2 to 15%, respectively. A commercially available Pt based DOC showed good CO and HC light-off performance at 500 ppm of CO and HC at up to 10% O2. However, it did not keep the superior light-off activity when CO and HC were increased to 5,000 ppm and O2 was decreased to 2%. A commercially available Pt-Pd based DOC demonstrated better light-off activity compared to the Pt based DOC at lower CO and HC concentrations.