Adhesive Bonding Performance of GA Coated 590 MPa Tensile Strength Steels
2011-04-12
2011-01-1052
Advanced high strength steels (AHSS) are becoming major enablers for vehicle light weighting in the automotive industry. Crash resistant and fracture-toughened structural adhesives have shown potential to improve vehicle stiffness, noise, vibration, and harshness (NVH), and crashworthiness. They provide weight reduction opportunity while maintaining crash performance or weight increase avoidance while meeting the increasing crash requirement. Unfortunately, the adhesive bonding of galvanneal (GA)-coated steels has generally yielded adhesive failures with the GA coating peeling from the steel substrate resulting in poor bond strength. A limited study conducted by ArcelorMittal and Dow Automotive in 2008 showed that GA-coated AHSS exhibited cohesive failure, and good bond strength and crash performance. In order to confirm the reliable performance, a project focusing on the consistency of the adhesive bond performance of GA-coated steels of 590 MPa strength level was initiated.