Titanium’s high strength-to-weight ratio and corrosion resistance makes it ideal for many aerospace applications, especially in heat critical zones. Superplastic Forming (SPF) can be used to form titanium into near-net, complex shapes without springback. The process uses a machined die where inert gas is applied uniformly to the metal sheet, forming the part into the die cavity. Standard titanium alpha-beta alloys, such as 6Al-4V, form at temperatures between 900 and 925°C (1650-1700°F). Recent efforts have demonstrated alloys that form at lower temperatures ranging between 760 and 790°C (1400-1450°F). Lowering the forming temperature reduces the amount of alpha case that forms on the part, which must be removed. This provides an opportunity of starting with a lower gauge material. Lower forming temperatures also limit the amount of oxidation and wear on the tool and increase the life of certain press components, such as heaters and platens.

Titanium is a difficult material to fabricate into complex configurations. There is several elevated temperature forming processes available to produce titanium components for aerospace applications. The processes to be discussed are Superplastic Forming (SPF), hot forming and creep forming. SPF uses a tool that contains the required configuration and seals around the periphery so inert gas pressure can be used to form the material. Of the processes to be discussed, this is the one that can produce the most complex shapes containing the tightest radii. A variation of the process combines an SPF operation with diffusion bonding (SPF/DB) of two or more pieces of titanium together to produce integrally stiffened structure containing very few fasteners. Another process for shaping titanium is hot forming. In this process, matched metal tools, offset by the thickness of the starting material, are used to form the part contour at elevated temperature.