Search Results

Electrical steel, also known as silicon steel, is a ferromagnetic material that is often used in electric vehicles (EVs) for stator and rotor applications. Since the design and manufacturing of rotors require the use of laminated thin electrical steel sheets, the fatigue characterization of these single sheets is of interest. In this study, a 0.27mm thick non-oriented electrical steel sheet was tested under cyclic loading in the load-controlled mode with the load ratio R = 0.1 at room temperature. The specimens were prepared using the Computer Numerical Control (CNC) machining method. The Smith-Watson-Topper mean stress correction was used to find the equivalent fully reversed stress-life (S-N) curve. The Basquin equation was used to describe the fatigue strength of the electrical steel and the fatigue parameters were extracted. Furthermore, a design curve with a reliability of 90% and a confidence level of 90% was generated using Owen’s Tolerance Limit method.

The Self-Piercing Rivet (SPR) is an effective method for joining aluminum sheets and dissimilar materials. The durability assessment of SPR joints is essential for the optimum design of the automotive body-in-white structure. Fatigue analysis is required for any structural system subject to cyclic loading where durability assessment is required. While there is no established fatigue life prediction model for SPR joints, Rupp’s model is a well-established fatigue life prediction method intended for resistance spot welds. Rupp’s model has been the automotive industry’s choice for fatigue life estimation due to its computational efficiency and ability to capture various loading conditions. The purpose of this study is to investigate the compatibility of Rupp’s model with SPR joints. Load-control fatigue testing was conducted on cross-tension SPR joints of aluminum sheets (Al 6016) with dissimilar thicknesses and SPR joints of dissimilar materials (Al 6016 to DX54D steel).

Strict environmental regulations are driving the automotive industry toward electric vehicles as they offer zero emissions. A key component in electric vehicles is the electric motor, where the stator and rotor are manufactured from stacks of thin electrical steel sheets. The electrical steel sheets can be cut in different ways, and the cutting methods may significantly affect the fatigue strength of the component. It is important to understand the effect of the cutting processes on the fatigue properties of electrical steel to ensure there is no premature failure of the electric motor resulting from an improper cutting process. This investigation compared the effect of three different edge preparation methods (stamping, CNC machining, and waterjet cutting) on the fatigue performance of 0.27mm thick electrical steel sheets. To investigate the effect of the edge finish on fatigue behavior, surface roughness was measured for these different samples.

Electrical steels are silicon alloyed steels that possess great magnetic properties, making them the ideal material choice for the stator and rotor cores of electric motors. They are typically comprised of laminated stacks of thin electrical steel sheets. An electric motor can reach high temperatures under a heavy load, and it is important to understand the combined effect of temperature and load on the electrical steel’s performance to ensure the long life and safety of electric vehicles. This study investigated the fatigue strength and failure behavior of a 0.27mm thick electrical steel sheet, where the samples were prepared by a stamping process. Stress-control fatigue tests were performed at both room temperature and 150°C. The S-N curve indicated a decrease in the fatigue strength of the samples at the elevated temperature compared to the room temperature by 15-25 MPa in the LCF and HCF regimes, respectively.

Interest in magnesium, as the lightest engineering metal, has increased in the automotive industry as a result of requirements for lighter and cleaner vehicles. Resistance spot welding (RSW) is already the predominant mode of fabrication in this industry, and the fatigue of spot welded magnesium sheet must be studied. In this study, the tensile and fatigue strength of resistance spot welded AZ31 Mg alloy was studied. Three sets of tensile shear spot welded specimens were prepared with different welding parameters to achieve different nugget sizes. Metallographic examination revealed grain size changes from the base material (BM) to heat affected zone (HAZ) to the fusion zone (FZ). Monotonic tensile and fatigue tests were conducted and the effect of nugget size on tensile shear and fatigue strength was discussed.