By increasing the percentage of highly dissociative strong acid components included in the neutralizing acid of the electrodeposition coating, it was possible to improve electrical conductivity and coulomb efficiency and achieve excellent throwing power. The GA cratering caused by the increase in the strong acid ratio was resolved by setting the strong acid ratio to 90% while reducing MEQ. By increasing coulomb efficiency, the quantity of hydrogen gas produced during electrodeposition was minimized, and as a result, gas pinholes remaining in the coating were reduced, increasing the smoothness of the coating beyond than that of the current materials. As a result of this study, the usage of e-coating per vehicle body was reduced by approximately 11%.

A new liquid surface conditioner has been developed to improve phosphate coating quality and enable a low-temperature phosphating system designed to reduce CO₂ emissions during the pretreatment processes of automobile production. Phosphate film is formed by a phosphating treatment that provides corrosion resistance for the steel plates that make up auto bodies. In the vehicle body, pocket-shaped structures such as side sills and wheel arches are likely to collect muddy water and form rust. Regarding anticorrosion quality assurance, particular attention must be paid to these pocket structures, in which phosphating solution flows slowly, and a lower solution-volume-to-surface-area ratio contributes less to the phosphating reaction. For this reason, with the conventional liquid surface conditioner, a low-temperature phosphating system cannot coat substrate surfaces sufficiently, which would result in lower corrosion resistance.