More Mg alloys are being considered for uses in the automotive industry. Since the corrosion performance of Mg alloy components in practical service environments is unknown, long term corrosion testing at automotive proving grounds will be an essential step before Mg alloy components can be implemented in vehicles. However, testing so many Mg alloy candidates for various parts is labor intensive for the corrosion engineers at the proving grounds. This report presents preliminary results in evaluating corrosion performance of Mg alloys based on rapid corrosion and electrochemical tests in the lab. In this study, four Mg alloy candidates for transmission cases and oil pans: AE44, AXJ530, MRI153M and MRI230D were tested in the lab and at General Motors Corporation Milford Proving Ground and their corrosion results were compared.

AZ31B Mg sheet is being considered for automotive applications. This study investigates the effect of pre-treatments, such as heat-treatments and surface treatments, on the corrosion performance of AZ31B sheet, with a goal of learning which pre-treatment can improve corrosion resistance of the sheet material in production. It is found that the heat-treatment and oxidation during a warm and hot forming (WHF) process will not deteriorate the corrosion performance of the AZ31B sheet; polishing and acid etching can clean the surface and significantly increase the corrosion resistance, but corrosion can be accelerated by sandblasting which contaminates the surface. The change in corrosion performance can be associated with surface cleaning or contamination of the sheet by these pre-treatments. Furthermore, the influence of a pre-treatment on the uncoated AZ31B sheet may affect its corrosion behavior after coating.

Magnesium alloys are not corrosion resistant in many applications and they require coating protection. In this study, we developed an electroless E-coating technique for magnesium alloys and discussed a cathodic E-coating deposition mechanism for the electroless E-coating process. This coating can be formed within a few seconds by dipping a magnesium alloy (i.e., AZ91D) in an E-coat bath without applying a current or voltage. The deposited electroless coat can offer good protection to the AZ91D magnesium alloy in 5 wt% NaCl corrosive solution as well as in a phosphating bath. The most interesting finding is that the electroless coating is not sensitive to local damage. No preferential corrosion attack occurred along the scratches made on the coating.