Search Results

Strain controlled thermo-mechanical fatigue (TMF) tests were conducted on a high Silicon ductile cast iron (SiMo) as the baseline material and a similar SiMo cast iron with aluminum addition (SiMoAl). The much improved fatigue life with aluminum addition is analyzed using the integrated creep-fatigue theory (ICFT) in combination with the metallurgical analysis on the tested coupons. Addition of about 3 wt.% Aluminum significantly improved TMF life of the SiMo cast iron. The results are explained by elimination of brittleness at middle temperature range, the higher flow stress, lower creep rate and higher oxidation resistance from Al addition.

A novel Spatially Optimized Diffusion Alloy (SODA) material has been developed and applied to exhaust systems, which are an aggressive environment subject to high temperatures and loads, as well as excessive corrosion. Traditional stainless steels disperse chromium homogeneously throughout the material, with varying amounts ranging from 10% to 20% dependent upon its grade (e.g. 409, 436, 439, 441, and 304). SODA steels, however, offer layered concentrations of chromium, enabling an increased amount along the outer surface for much needed corrosion resistance and aesthetics. This outer layer, typically about 70μm thick, exceeds 20% of chromium concentration locally, but is less than 3% in bulk, offering selective placement of the chromium to minimize its overall usage. Since this layer is metallurgically bonded, it cannot delaminate or separate from its core, enabling durable protection throughout manufacturing processes and full useful life.

Selected ferritic stainless steel sheets for exhaust applications were tested under thermo-mechanical fatigue (TMF) condition in the temperature range of 400-800 °C with partial constraint. Straight welded tubes were used as the testing coupons to withstand large compression without buckling, and to understand the effect of welding as well. Repeated tests confirmed the observed failure scenario for each material type. The hysteresis loop behaviors were also simulated using the mechanism-based integrated creep and fatigue theory (ICFT) model. Although more development work is needed, for quick material screening purpose this type of testing could be a very cost effective solution for materials and tube weld development for exhaust applications.

The purpose of this work was to initiate a comparative evaluation of the aqueous corrosion resistance of ferritic stainless steels currently used to fabricate automotive exhaust systems. Both acid condensate and double loop electrochemical potentiokinetic reactivation (DL-EPR) testing using both as-received and heat treated test coupons prepared from Types 409, 409Al, 436 and 439 stainless steel was conducted for this purpose. A truncated version of an in-house acid condensate testing protocol revealed that Type 409Al stainless steel was the most resistant to corrosion of the four ferritic stainless steels examined, whereas Type 409 stainless steel was the least resistance to corrosion.

In this paper, both standard and constrained thermomechanical fatigue (TMF) tests were conducted on a high silicon ductile cast iron (DCI). The standard TMF tests were conducted with independent control of mechanical strain, out-of-phase (OP) and in-phase (IP) strain, and temperature in the range from 300 to 800°C. The constrained TMF tests were conducted with various constraint ratios of 100%, 70%, 60% and 50% at the temperature ranges of 160 to 600°C and 160 to 700°C. Based on a material model as calibrated with low-cycle fatigue (LCF) data of DCI, finite element analyses (FEA) of the above TMF tests were carried out with Abaqus. A damage mechanism-based lifetime model was integrated into a C++ API code to post-process the Abaqus output results. Simulation predictions show good agreement with experiments for stress-strain responses and lifetime under different TMF conditions.

Strain-controlled low-cycle fatigue (LCF) experiments were conducted on ductile cast iron at total strain rates of 1.2/min, 0.12/min and 0.012/min in a temperature range of RT ~ 800°C. An integrated creep-fatigue (ICF) life prediction framework is proposed, which embodies a deformation mechanism based constitutive model and a thermomechanical damage model. The constitutive model is based on the decomposition of inelastic deformation into plasticity and creep mechanisms, which can describe both rate-independent and rate-dependent cyclic responses under wide strain rate and temperature conditions. The damage model takes into consideration of i) plasticity-induced fatigue, ii) intergranular embrittlement, iii) creep and iv) oxidation. Each damage form is formulated based on the respective physical mechanism/strain.