The maximum equivalent plastic strain (EPSmax), which can be achieved in the gauge region of a cruciform specimen during in-plane biaxial tensile tests, is limited due to early fracture on the cruciform specimen arm. In this paper, a theoretical model was proposed to determine the factors related to the EPSmax of a cruciform specimen following ISO 16842: 2014. Biaxial tensile tests were carried out to verify the theoretical analyses. Results show that the material strength coefficient (k) has no effect on the EPSmax, and EPSmax increases with the increase of the material hardening exponent (n) and the cross-sectional-area ratio (c) of the arm region to the gauge region. It is found that the applied load ratio (α) has an effect on EPSmax, which decreases as the load ratio increases from 0:1 (i.e. uniaxial tension) to 1:2 (i.e. plane strain state) and then increases as the load ratio increases to 1:1 (i.e. balanced biaxial tension).

A comparison of welding techniques was performed to determine the most effective method for producing aluminum tailor-welded blanks for high volume automotive applications. Aluminum sheet was joined with an emphasis on post weld formability, surface quality and weld speed. Comparative results from several laser based welding techniques along with friction stir welding are presented. The results of this study demonstrate a quantitative comparison of weld methodologies in preparing tailor-welded aluminum stampings for high volume production in the automotive industry. Evaluation of nearly a dozen welding variations ultimately led to down selecting a single process based on post-weld quality and performance.

The preform annealing process is a two-stage stamping method for shaping non age-hardenable (i.e. 5000 series) aluminum sheet panels in which the panel is heat treated in between the two steps to improve overall formability of the material. The intermediate annealing heat treatment eliminates the cold work accumulated in the material during the first draw. The process enables the ability to form more complex parts than a conventional aluminum stamping process. A demonstration of local annealing for this process was conducted to form a one-piece aluminum liftgate inner panel for a large sport utility vehicle using the steel product geometry without design concessions. In prior work, this process was demonstrated by placing the entire panel in a convection oven for several minutes to completely anneal the cold work.