Search Results

Lightweight metals such as Al and Mg alloys have been increasingly used for reducing mass in both structural and non-structural applications in transportation industries. Joining these lightweight materials using traditional fusion welding techniques is a critical challenge for achieving optimum mechanical performance, due to degradation of the constituent materials properties during the process. Friction stir welding (FSW), a solid-state joining technique, has emerged as a promising method for joining these lightweight materials. In particular, high joining efficiency has been achieved for FSW of various Al alloys and Mg alloys separately. Recent work on FSW of dissimilar lightweight materials also show encouraging results based on quasi-static shear performance. However, coach-peel performance of such joints has not been sufficiently examined.

Friction stir linear welding (FSLW) is widely used in joining lightweight materials including aluminum alloys and magnesium alloys. However, fatigue life prediction method for FSLW is not well developed yet for vehicle structure applications. This paper is tried to use two different methods for the prediction of fatigue life of FSLW in vehicle structures. FSLW is represented with 2-D shell elements for the structural stress approach and is represented with TIE contact for the maximum principal stress approach in finite element (FE) models. S-N curves were developed from coupon specimen test results for both the approaches. These S-N curves were used to predict fatigue life of FSLW of a front shock tower structure that was constructed by joining AM60 to AZ31 and AM60 to AM30. The fatigue life prediction results were then correlated with test results of the front shock tower structures.

We characterize the cyclic behavior of an AM30 extruded magnesium alloy. The micromechanisms of cyclic damage were studied by means of strain controlled experiments in both the extruded and transverse directions. A scanning electron microscope (SEM) analysis of the microstructure revealed that second phase particles were present in the Mg alloy that nucleated the cracks. However, crack initiation sites were observed to occur due to profuse twinning. Low cycle fatigue parameters were determined, and a microstructure-sensitive MultiStage Fatigue (MSF) model, which is able to capture mechanical and microstructure properties, was implemented to predict fatigue behavior and failure.

Magnesium alloys are the lightest structural metal and recently attention has been focused on using them for structural automotive components. Fatigue and durability studies are essential in the design of these load-bearing components. In 2006, a large multinational research effort, Magnesium Front End Research & Development (MFERD), was launched involving researchers from Canada, China and the US. The MFERD project is intended to investigate the applicability of Mg alloys as lightweight materials for automotive body structures. The participating institutions in fatigue and durability studies were the University of Waterloo and Ryerson University from Canada, Institute of Metal Research (IMR) from China, and Mississippi State University, Westmorland, General Motors Corporation, Ford Motor Company and Chrysler Group LLC from the United States.