Search Results

Ferritic nitrocarburizing offers excellent wear, scuffing, corrosion and fatigue resistance by producing a thin compound layer and diffusion zone containing ε (Fe2-3(C, N)), γ′ (Fe4N), cementite (Fe3C) and various alloy carbides and nitrides on the material surface. It is a widely accepted surface treatment process that results in smaller distortion than carburizing and carbonitriding processes. However this smaller distortion has to be further reduced to prevent the performance issues, out of tolerance distortion and post grinding work hours/cost in an automotive component. A numerical model has been developed to calculate the nitrogen and carbon composition profiles of SAE 1010 torque converter pistons during nitrocarburizing treatment. The nitrogen composition profiles are modeled against the part thickness to predict distortion.

Carburized parts often see use in powertrain components for the automotive industry. These parts are commonly quenched and tempered after the carburizing process. The present study compared the austempering heat treatment to the traditional quench-and-temper process for carburized parts. Samples were produced from SAE 8620, 4320, and 8822 steels and heat treated across a range of conditions for austempering and for quench-and-tempering. Distortion was examined through the use of Navy C-Ring samples. Microstructure, hardness, and Charpy toughness were also examined. X-ray diffraction was used to compare the residual stress found in the case of the components after the quench-and-temper and the austempering heat treatments. Austempering samples showed less distortion and higher compressive residual stresses, while maintaining comparable hardness values in both case and core. Toughness measurements were also comparable between both processes.

Nitrocarburizing is an economical surface hardening process and is proposed as an alternative heat treatment method to carbonitriding. The focus of this study is to compare the size and shape distortion and residual stresses resulting from the ferritic nitrocarburizing and gas carbonitriding processes for SAE 1010 plain carbon steel. Gas, ion and vacuum nitrocarburizing processes utilizing different heat treatment temperatures and times were performed to compare the different ferritic nitrocarburizing processes. Navy C-Ring specimens and prototype stamped parts were used to evaluate size and shape distortion. X-ray diffraction techniques were used to determine the residual stresses in the specimens. Overall, the test results indicate that the nitrocarburizing process gives rise to smaller dimensional changes than carbonitriding, and that the size and shape distortion can be considerably reduced by applying appropriate ferritic nitrocarburizing procedures.

SAE 8620 and other steels are typically used in the carburized condition for powertrain applications in the automotive industry, i.e., differential ring gears, camshafts, and transmission gears. Although current recommended carburizing practice involves normalizing the steel prior to carburizing, elimination of this normalizing treatment could lead to significant cost reductions. This research examines whether the normalizing process prior to carburizing could be eliminated without negatively affecting part performance. This study focused on the effects of the initial microstructure on the residual stress, retained austenite, and effective case depths of carburized SAE 8620 and PS-18 steels.

The focus of this study was to determine the residual stress and retained austenite profiles for carbonitrided and nitrocarburized SAE 1010 plain carbon steel and to relate these profiles to one another and to the distortion resulting from heat treatment. Navy C-ring specimens were used for the purpose of this study and X-ray diffraction techniques were used to measure both residual stress and retained austenite. The findings from this research are then applied to a manufacturing application involving the surface hardening of a thin shelled, plain carbon steel automotive component.

Steels such as SAE 8620 and PS-18 are typically used in the carburized condition for powertrain applications in the automotive industry. Such steels always contain retained austenite to varying degrees in both the ashardened and tempered microstructures. As well as retained austenite, heat treatment can produce residual stresses, which lead to both size and shape distortions. The intent of this study was to investigate the effects of initial microstructure, composition, and heat treatment on the amount of residual stress, retained austenite, and distortion in carburized SAE 8620 and PS-18 steels. A specially designed specimen, the Navy C-ring, was used to evaluate distortion. X-ray diffraction techniques were used to determine the residual stress and the amount of retained austenite.