Composite bearings of PTFE as the base material have been widely used for automotive parts. However, in recent years, due to downsizing, faster sliding speeds, and tendency to increase the bearing load with high performance, particularly for boundary lubrication conditions, the PTFE-based composite bearing is often worn, making it difficult to apply to some applications. A high strength polymer was selected as an alternative to PTFE base material, and the mechanical properties and performance in a start-stop test, reciprocating sliding test and seizure test were evaluated. Focusing on the characteristics of high strength, by applying a PEEK resin, in each evaluation, it was confirmed that superior performance was achieved compared with a conventional PTFE based composite bearing.

Resin-based overlays as lead-free bearing materials for automobile engines are experimentally studied using tribology testing apparatus and an engine bench test rig. A resin overlay newly proposed is composed of Polybenzimidazole (PBI) as the base resin and solid lubricant Molybdenum disulfide (MoS2) as an additive. PBI has high temperature performance and good adhesion and physical strength under higher temperatures. Consequently, a PBI-based overlay has good sliding properties in terms of wear resistance and fatigue resistance. The resin overlay shows applicability to automobile engine bearings which are used under high loads.