The advent of more efficient direct injection turbocharged engines has increased the need for higher performance connecting rods, able to withstand in particular higher compressive loads in operation. In this respect, new high strength materials for powder forged connecting rods were developed and introduced in production with excellent results. Among them, HS170M is currently used to manufacture connecting rods for several high performance engines, which not only have higher strength, but have less variation in their mechanical properties. The results of numerous benchmark studies have shown that powder forged connecting rods manufactured with HS170M are stronger than their steel forged counterparts manufactured with microalloyed steels, are easier to machine and fracture split, and represent a cost effective way to manufacture this important high reliability automotive component.

Over the last two decades, powder forging (PF) has been proven as a very reliable way to successfully manufacture connecting rods for both gasoline and diesel applications. The inherent value in the near net formed product (NVH performance, material utilization efficiency, total cost economics) coupled with the attractive strength levels achieved with the introduction of HS150, HS160, and HS170 materials [1, 2, 3], have made it possible for PF connecting rods to meet and exceed the increasing performance specifications required by the next generation of diesel and gasoline engines. The goal of this work was to continue the research performed so far in developing new higher strength materials for PF connecting rods [1, 2, 3, 4, 5, 6] in order to further optimize the chemical composition of Fe-Cu-C systems for maximum performance.

The main requirement for the satisfactory function and service life of a connecting rod is the fatigue strength, which is dependent on design, material, microstructure, and surface condition. Much work has been accomplished to study and optimize these factors in the case of powder forged connecting rods [1, 2, 3, 4, 5, 6, 7 and 8]. To meet the current and increasing performance specifications required by the next generation of diesel and gasoline engines, new high strength powder forged materials have been introduced into production to successfully compete with wrought steels [9, 10, 11 and 12]. Currently, there are two main processing technologies available to manufacture connecting rods: fracture-split drop forging and fracture-split powder forging. The cost effectiveness of each one of these technologies is another main consideration, other than performance, in high volume production.