Search Results

The first-ever application of a hydrogen-free diamond-like carbon (H free DLC) coating to a mass-production gasoline engine reduces friction between the cylinder bore and piston by 18%. It is explained the reducing friction effect of H free DLC by oil film thickness of piston ring. When H-free DLC is applied to top ring, friction is over 10% reduced. Because low friction coating is effective in a thin oil film at a large area near top dead center (TDC). It is also found that the friction reduction effect is enhanced when low viscosity engine oil is used. DLC as a low friction coating is more effective in a thinner oil film. In this study, the adhesion strength of H-free DLC coating on piston rings is improved because of providing a smooth substrate, the new washing process and the optimized coating characteristics. Adhesion strength is verified by test results using actual parts considered to contribute to piston ring load.

Due to its lower friction property, a hydrogen-free diamond-like carbon coating (DLC) obtained by an ion-plating physical vapor deposition (PVD) process as an amorphous carbon film (a-C) was applied to an engine valve lifter to reduce mechanical losses. The effect of the a-C coating on reducing friction was evaluated with an engine motoring tester using actual engine parts. To meet the specifications of the valve lifter, a study was made of the typical topography of the a-C coating surface profile and the effect of the film thickness against abrasive wear.

One important development area for obtaining better fuel economy is to reduce mechanical friction losses in engine components. The valvetrain is a significant source of mechanical friction loss in an automobile engine, especially at low speeds where fuel economy is most important. This paper describes the potential use of diamond-like carbon (DLC) coatings at the cam/follower interface in a bucket-type valvetrain. Using a pin-on-disk tester, a motored valvetrain friction apparatus and a bench test rig, the frictional performance of DLC coatings was tested. Experimental data indicate that under a lubricated condition, DLC coatings produced by a plasma CVD (chemical vapor deposition) technique did not show a sufficient effect on reducing friction (only a 20-25% reduction) contrary to our expectations. DLC coatings prepared by arc-ion plating and containing less hydrogen showed superior frictional performance compared with CVD-DLC coatings under a lubricated condition.

The mechanism causing the micro slip characteristic of a metal CVT belt during torque transmission was analyzed, focusing on the gap distribution between the elements. It was hypothesized that gaps between the elements cause slip to occur between the elements and the pulleys when the belt is squeezed between the two halves of the pulleys, and the slip ratio was calculated theoretically on that assumption. The μ-v (friction coefficient versus sliding velocity) characteristic between the elements and the pulleys was measured and the results were used in calculating the slip ratio. As a result, a simulation procedure was developed for predicting the slip-limit torque of the belt on the basis of calculations. The slip ratio found by simulation and the calculated slip-limit torque showed good quantitative agreement with the experimental data, thereby confirming the validity of the simulation procedure.