High-strength aluminum alloys such as 7075 can be formed using advanced manufacturing methods such as hot stamping. Hot stamping utilizes an elevated temperature blank and the high pressure stamping contact of the forming die to simultaneously quench and form the sheet. However, changes in the thermal history induced by hot stamping may increase this alloy’s stress corrosion cracking (SCC) susceptibility, a common corrosion concern of 7000 series alloys. This work applied the breaking load method for SCC evaluation of hot stamped AA7075-T6 B-pillar panels that had been artificially aged by two different artificial aging practices (one-step and two-step). The breaking load strength of the specimens provided quantitative data that was used to compare the effects of tensile load, duration, alloy, and heat treatment on SCC behavior.

Increasing fuel economy is a high priority of the automotive industry due to consumer demand and government regulations. High strength aluminum alloys such as AA7075-T6 can be used in strength-critical automotive applications to reduce vehicle weight and thus improve fuel economy. However, these aluminum alloys are known to be susceptible to stress corrosion cracking (SCC) for thick plate. The level of susceptibility to SCC must be determined before a material is implemented. ASTM standards exist that generate semi-quantitative data primarily for use in screening materials for SCC. For the purposes of this work ASTM G139 (breaking load method) has been used to evaluate sheet AA7075-T6 for use in automotive applications. A tensile fixture applying a constant strain was used to quantitatively measure residual strength of the material after exposure to a corrosive environment.

A compact in-situ tensile stress fixture was designed for the study of the combined effects of stress and automotive environments on structural glass fiber-reinforced composite materials. With this fixture, a standardized 300 hour laboratory screening test was developed to compare the residual property loss of composite materials due to concurrent exposure to stress and environment. It is of great importance that the data gathered in the laboratory have correlation to on-vehicle (in-service) performance, and that both lab and real world data be taken with a test system (in-situ test fixtures) capable of providing accurate and consistent results under either test condition.