Weld lines can significantly reduce ultimate tensile strength (UTS) and fracture strain of talc filled polypropylene (PP). In this paper, two different injection molding tests were completed. First, an injection mold with triangular inserts was built to study the influence of meeting angles on material properties at the weld line region. Tensile samples were cut at different locations along the weld line on the injection molded plaques. The test results showed that both UTS and fracture strain increase when the sample locations are away from the insert. This trend is attributed to different meeting angles. Second, standard ISO tensile bars with and without weld line were injection molded to identify the size of the weld line affected zone. A FEA model was built in ABAQUS, where the tensile sample was divided into two different regions, the solid region and the weld line affected region.

Warpage is the distortion induced by inhomogeneous shrinkage during injection molding of plastic parts. Uncontrolled warpage will result in dimensional instability and bring a lot of challenges to the mold design and part assembly. Current commercial simulation software for injection molding cannot provide consistently accurate warpage prediction, especially for semi-crystalline thermoplastics. In this study, the root cause of inconsistency in warpage prediction has been investigated by using injection molded polypropylene plaques with a wide range of process conditions. The warpage of injection molded plaques are measured and compared to the numerical predictions from Moldex3D. The study shows that with considering cooling rate effect on crystallization kinetics and using of the improved material model for residual stress calculations, good agreements are obtained between experiment and simulation results.

Weld lines occur when melt flow fronts meet during the injection molding of plastic parts. It is important to investigate the weld line because the weld line area can induce potential failure of structural application. In this paper, a weld line factor (W-L factor) was adopted to describe the strength reduction to the ultimate strength due to the appearance of weld line. There were two engineering thermoplastics involved in this study, including one neat PP and one of talc filled PP plastics. The experimental design was used to investigate four main injection molding parameters (melt temperature, mold temperature, injection speed and packing pressure). Both the tensile bar samples with/without weld lines were molded at each process settings. The sample strength was obtained by the tensile tests under two levels of testing speed (5mm/min and 200mm/min) and testing temperatures (room temperature and -30°C). The results showed that different materials had various values of W-L factor.