Search Results

Impact toughness (or resistance to fracture) is a key material property for press hardened steel used in construction of the safety-critical elements of automotive body structures. Prior austenite grain size, as primarily controlled by the incoming microstructure and austenitization process, is a key microstructural feature that influences the impact toughness of press hardened steel. In this paper, a special Charpy V-notch impact test is developed to quantify the impact toughness of press hardened steel sheets with various prior austenite grain sizes, by stacking a number of thin sheets via mechanical riveting. Both the ductile-to-brittle transition temperature and upper shelf energy are analyzed in an effort to establish a correlation between impact toughness and prior austenite grain size. Within tested conditions, impact performance shows only a slight decrease as the prior austenitic grain size increases from 18 to 38 microns.

Press hardened steels (PHS) are commonly used in automotive structural applications because of their combination of extremely high strength, load carrying capacity and the ability to form complex shapes in the press hardening process. Recent adoption of increased roof crush standards, side impact requirements and the increased focus on CO2 emissions and mass reduction have led autmotive manufacturers to significantly increase the amount of PHS being designed into future vehicle designs. As a way to further optimize the use of these steels, multi-gauge welded blanks of PHS and multi-material blanks of PHS to microalloyed steels of various thickness have been developed to help achieve these requirements. More recently, tailor rolled PHS, whereby the steel is rolled such that the thickness changes across the width of the sheet, have been developed.

Drop tower axial crush testing was performed on hat section samples of various steel grades ranging in minimum tensile strength from 410 MPa to 1300 MPa. It was demonstrated that the energy absorption capability increases with the tensile strength of the steel. However, steels of very high strength, greater than 980 MPa tensile strength, exhibited a greater tendency for weld button pullout or material fracture, and thus limited energy the absorption capability. The effect of the closeout plate and the yield strength of the steel on energy absorption were also investigated. FEA simulations were performed and correlated to the experimental results. A flow stress based material criterion is introduced based on the analytical approach to compare the crush performance of steels.

In the first part of this paper, a previously published acceleration compensation methodology for dynamic dent testing [1] was successfully applied to calculate dent loads and applied energy in dynamic dent testing. This procedure was validated utilizing a hydraulic controlled dynamic dent tester on a number of low carbon and bake hardenable steels. In the second part of this study, the impact of strain rate on material bending and hardening in high-speed dynamic dent resistance testing was studied. Previous work [2] investigated these factors in static dent resistance. The procedure utilized in that research was further developed and adapted for high speed testing and used as a basis for a new, single loading incremental dynamic dent test. This new test was used to investigate the effects of material bending and hardening in high-speed dynamic dent resistance. Testing incorporated laboratory produced stretch dome panels with 2% biaxial strains as test specimens.

A standardized quasi-static dent test has been used in evaluating the dent resistance of automotive body panels for many years. In order to predict the onset of a visible dent, cyclic loading with small load increments was adopted into standard automotive test procedures. Although researchers have investigated the effects of sheet thickness, yield strength, strain aging and prestrain on the static dent resistance of sheet steel in the past, material bending and hardening effects on static dent resistance were assumed to be inconsequential, and were therefore largely ignored. In this study, the impacts of material bending and hardening on static dent resistance are investigated. A fixed load, single loading condition was carefully designed for different materials and incorporated into the quasi-static dent test. For comparison, the incremental quasi-static loading condition is also examined.